Abstract:Purpose This paper aims to investigate the corrosion kinetics and corrosion behavior of NdFeB magnets with the addition of heavy rare earth dysprosium (Dy) for its inhibitory activity on poor corrosion resistance of NdFeB magnets. Design/methodology/approach To study the effect of dysprosium addition on corrosion behavior of NdFeB magnets and investigate its mechanism, potentiodynamic polarization, scanning electron microscopy (SEM), electrochemical impedance, energy dispersion spectrum (EDS) and scanning Kelvin probe force microscopy (SKPFM) were applied in the research. Besides, microstructures were observed by SEM equipped with EDS. Atomic force microscopy was introduced to analyze the morphology, potential image as well as the contact potential difference. The SKPFM mapping scan was applied to obtain the contact potential around Nd-rich phase at 0.1 Hz. The magnets were detected via X-ray diffraction. Findings Substitution of Nd with Dy led to improvement of corrosion resistance and reduced the potential difference between matrix and Nd-rich phase. Corrosion resistance is Nd-rich phase < the void < metal matrix; maximum potential difference between matrix and Nd-rich phase of Dy = 0, Dy = 3 and Dy = 6 Wt.% is 411.3, 279.4 and 255.8 mV, respectively. The corrosion rate of NdFeB magnet with 6 Wt.% Dy is about 67% of that without Dy at steady corrosion stage. The addition of Dy markedly enhanced the corrosion resistance of NdFeB magnets. Originality/value This research innovatively investigates the effect of adding heavy rare earth Dy to NdFeB permanent magnets on magnetic properties, as well as their effects on microstructure, phase structure and most importantly on corrosion resistance. Most scholars are studying the effect of element addition on magnetic properties but not on corrosion resistance. This paper creatively fills this research gap. NdFeB magnets are applied in smart cars, robotics, AI intelligence, etc. The in-depth research on corrosion resistance by adding heavy rare earths has made significant and outstanding contributions to promoting the rapid development of the rare earth industry.

ELECTROCHEMICAL CORROSION BEHAVIOR OF COMPONENT PHASES OF NdFeB MAGNET

Study Magnetic Properties and Corrosion Resistance of Sintered NdFeBAlDyNb Magnets

Corrosion behavior of Nd-Fe-B sintered magnets at remanence state

Towards Peculiar Corrosion Behavior of Multi-Main-phase Nd-Ce-Y-Fe-B Permanent Material with Heterogeneous Microstructure

Corrosion Protection of Nd-Fe-B Sintered Magnets by Aluminum Coating

Corrosion Behavior of Hot-Pressed Nanocrystalline Ndfeb Magnet in A Simulated Marine Atmosphere

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Crucial Role of the REFe2 Intergranular Phase on Corrosion Resistance of Nd-La-Ce-Fe-B Sintered Magnets

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

Corrosion resistance and mechanical properties of (Ho,Nd)FeB magnets

A design of sintered Nd-Fe-B magnet exhibiting superior corrosion resistance based on the metallurgical behavior of Ni and Cr

Electrochemical Corrosion Behavior of Hot-Deformed NdFeB Magnet with Different Content of Nano-Tic

Amorphous Al–Mn Coating on NdFeB Magnets: Electrodeposition from AlCl3–EMIC–MnCl2 Ionic Liquid and Its Corrosion Behavior

Rare earth passivation and corrosion resistance of zinc coated NdFeB magnets

CATHODIC ELECTREPHORESIS PROCESS FOR BONDED NdFeB

Influence of dysprosium addition on corrosion behavior of NdFeB magnets

A Novel Anodic Electrophoresis Process for NdFeB Permanent Magnets

Diffusion of Nd-Rich Phase in the Spark Plasma Sintered and Hot Deformed Nanocrystalline Ndfeb Magnets

Corrosion Behavior of Sintered CeNdFeB Magnets in Different Solutions

A New Phase in Nd-Fe-B Sintered Magnets and Its Effect on Coercivity

Comparison of the corrosion resistances of chromium-passivated and cerium-passivated Zn/NdFeB magnets