High-pressure Synthesis and Properties of CeO 2 -Zro 2 Solid Solution

Dapeng Xu,Quanyong Wang,Zhe Lu,Zhiguo Liu,Gongmu Zhang,Wenhui Su
DOI: https://doi.org/10.1007/bf02900427
2001-01-01
Chinese Science Bulletin
Abstract:Using nanoparticles of CeO2 and ZrO2 prepared by the chemical precipitation method as starting materials, the singlephase cubic Ce0.5Zr0.5O2 solid solution (cCe0.5Zr0.5O2) has been synthesized under 3.1 GPa at 1073 K for the first time. The structure of the c-Ce0.5Zr0.5O2 has not been changed before and after annealing at 773 K for 1 h. Only an unknown EPR signal (g =1.990) has been observed in the c-Ce0.5Zr0.5O2 and not varied after annealing at 773 K for 1 h, which exhibited that there exists no Ce3+ in the c-Ce0.5Zr0.5O2 and the Ce4+ has not been reduced into Ce3+ after annealing. The transport mechanism is ionic for the c-Ce0.5Zr0.5O2. The bulk conductivity (σ =1.2 ×10−5 S/cm at 823 K, σ=2.1 × 10−3 S/cm at 1123 K) is the same as that of CeO2, but smaller than that of Y2O3-stabilized ZrO2. A marked curvature at T = 823 K has been observed in the Arrhenius plot of the bulk conductivity. The activation energy below 823 K is lower than that above 823 K, and the reason has been discussed.
What problem does this paper attempt to address?