Abstract:Thermal stability of laser-modified surfaces is crucial for hot working conditions. Refined grain structure from the rapid solidification can only withstand a limited temperature range before the grain structure merges from grain boundary movement. Although the superior hardness properties are achievable through laser cladding, laser-clad surfaces are prone to cracking due to a mismatch in thermal expansion coefficient and coarse, hard particle size addition. Thus, this paper presents the thermal stability of laser-clad H13 tool steel with fine tungsten carbide (WC) particles (1-5 μm) addition to obstruct grain boundary movement and retain the refined grain structure. Controlled parameters for WC particle settlement onto H13 steel are laser power, pulse repetition frequency (PRF) and scanning speed. A thermal fatigue test was conducted on the clad surface for 1000-5000 cycles. The thermally worn clad surfaces were characterised for subsurface hardness properties, surface morphology and topography. The findings suggest the addition of WC particles during H13 steel surface melting increases the hardness properties to 2389 HV. Although the total volume of eroded surface and crack propagation responds evidently to the fatigue cycles, the refined grain structure is primarily intact, thus retaining the surface properties under high working temperatures. The WC particles observed amongst dendrite structure after 5000 cycles of fatigue test signify thermal stability at temperatures above 600°C. The thermal model anticipated higher stress distribution on the WC particles clad surface relative to the H13 steel substrate. These findings indicate fine particles' significance in strengthening grain structure for designing a prolonged dies surface life cycle.

High Power Laser Cladding Stellite 6+wc with Various Volume Rate by Duel Powder Feeding

Laser Cladding Stellite 6 + WC

Effect of Process Parameters on Microstructure and Properties of AlCoCrFeNi-WC-WS2 Composite Coating Prepared by Laser Cladding

Microstructural evolution in high power laser cladding of Stellite 6+WC layers

Microstructure Evolution of Stellite 6+wc by High Power Laser Cladding

Preparation of WC/Co Powders by Electroless Plating and Its Coating on 2cr13 Stainless Steel by Laser Cladding

Microstructure and Property of Laser Cladding Ni-based Alloy Coating Reinforced by WC Particles

Effect of WC content on microstructure and properties of high-speed laser cladding Ni-based coating

Thermal Stability of Laser-Clad Tool Steel with Fine Tungsten Carbide Particle Addition

WC-304 Powder/Screen Laser Composite Cladding Process and Simulation Research

Laser Cladding of Stellite and WFIC Series Cobalt Based Alloy Powder

Effect of Y2O3 Content on Microstructure and Wear Resistance of Laser Cladding Layer of Stellite-6 Alloy

Effect of WC on microstructure, molten pool and properties of Ni based coatings by multi-layer laser cladding

Study of Microstructure and Properties of Laser Cladding Ni60-WC + TiC Composite Coating

Analysis of Microstructure and Performance of Laser Cladding WC-Fe316L Alloy on the Surface of 27SiMn Steel

Effect of Powder Size and Volume Fraction of WC on the Microstructure of Laser Cladding WC-NiCrBSi Composite Coatings

Investigation on the Ni60-WC composite coatings deposited by extreme-high-speed laser-induction hybrid cladding technology: Forming characteristics, microstructure and wear behaviors

Effect of processing parameters on the microstructure of laser-clad Stellite 6 on the X19CrMoNbVN11-1 stainless-steel substrate

Effect of Preheating Temperature on Geometry and Mechanical Properties of Laser Cladding-Based Stellite 6/WC Coating

Microstructure and Properties of WC/Ni-Based Laser-Clad Coatings with Different WC Content Values

Microstructure, hardness and slurry erosion-wear behaviors of high-speed laser cladding Stellite 6 coatings prepared by the inside-beam powder feeding method