Abstract:The growth mechanism and morphologies of AlN whiskers prepared by the carbothermal reduction method are studied as well as the technological condition. All experiments were carried out in a vertical, controlled-atmosphere, graphite element resistance furnace. The reactor chamber volume is Φ250×210 mm, and the reactant weight is about 20 g each times (it contains about 70 wt.% Al2O3). Nitrogen pressure in the furnace is 0.1 MPa (1 atm). The optimum growth condition is at 1700°C for 5 h with flowing nitrogen (0.6 l min−1), when the raw materials are α-Al2O3 and graphite (Al2O3:C=4:1 in weight). The yield of AlN whiskers is about 3–5 g each time, and 50 wt.% or more of Al2O3 can convert to AlN whiskers. Generally, whiskers with hexagonal cross section grow along 〈0001〉 and plate-like whiskers have a growth orientation parallel to 〈0111〉 et al other than 〈0001〉. During the growth of whiskers, the VLS mechanism and VS mechanism serve the function together. In the early stage, α-Al2O3 will react with CaO to form Ca-aluminates such as CaO·6Al2O3(CA6), CaO·2Al2O3(CA2), CaO·Al2O3 (CA). These Ca-aluminates can provide liquid catalysts for the nucleation of AlN whiskers. After that, the AlN whiskers will grow out from the substrate surface by the VS mechanism. As proximity to substrate surface, there is less growth space and higher supersaturation, and far from substrate surface, there is large growth space and low supersaturation. So near the substrate surface AlN whiskers are small and with irregular shape. Far from the substrate surface, AlN whiskers are sensibly straight and with regular shape.

Fabrication of High Purity AIN Whisker

Fabricaion process and growth characteristics of A1N whiskers by sublimation-recrystallization method

Growth and Microstructure of Aln Whiskers and Dendrites

Synthesize Of Aluminum Nitride Whiskers By Carbothermal Reduction

Formation of AlN whiskers by nitridation of Al/AlN powders

Structure Characteristics of AlN Whiskers Fabricated by the Carbo-Thermal Reduction Method

Growth of aluminium nitride whiskers by sublimation-recrystallization method

Combustion Synthesis of AlN Whiskers

Morphology-controlled Synthesis of Hexagonal AlN Whiskers by Direct Nitridation of Aluminum and Alumina Mixture

Thermodynamics and Kinetic Considerations behind the Growth of AlN Whiskers Synthesized by Carbothermal Reduction

Morphologies and Growth Mechanisms of Aluminum Nitride Whiskers Synthesized by Carbothermal Reduction

Facile solvent-free synthesis of pure-phased AlN nanowhiskers at a low temperature

Formation Mechanism and Photoluminescence of Aln Nanowhiskers

A New Route to Synthesize SiC−AlN Solid Solution Whiskers

Influence of Al 2 O 3 · XH 2 O Crystallinities on the Morphology of AlOOH Whiskers

Toughening effect and mechanisms of AlN whiskers on a low‐temperature sintered AlNw/AlN ceramics

Synthesis Of Nbc Whiskers Having Dendrite Structure

Investigation On Combustion Synthesis Of Aln Whisker

Fabrication of Al-Ni nanofibers by selective etching

Morphologies and growth mechanisms of aluminium nitride whiskers

Bicrystal AlN Zigzag Nanowires