Abstract:The transformation-assisted consolidation under pressure has been demonstrated to be a promising method to fabricate the nano or submicron polycrystalline ceramic materials. The high pressure suppresses the long-range diffusion of the atoms and, consequently, restrains the grain coarsening. The new phases produced at high pressure could show finer grains under the appropriate thermodynamic conditions, which are not subject to the grain size of the raw materials. Ceramic materials exhibit the existence of the transformations under certain thermodynamic conditions and the formation of new phases generally undergoes the nucleation and growth. In the present work, monoclinic microcrystal ZrO2 with average grain size of 2 µm and Y2O3 with average grain size of 50 nm were mixed in molar ratio of 97∶3. The preparation of the samples was carried out by sintering at 5.5 GPa and temperatures of 800–1700 °C using the high pressure cubic cell, and the sample characterization was performed via the X-ray diffraction, scanning electron microscope and transmission electron microscopy. It was found that the monoclinic and submicron tetragonal composite polycrystalline ZrO2 in bulk is obtained under high pressure and high temperature. The average grain size of tetragonal ZrO2 fabricated at 1200, 1400, 1600 and 1700 °C is (145±62) nm, (246±165) nm, (183±62) nm and (245±107) nm, respectively. The synthesis of the fine-grained polycrystalline materials by the transformation under high pressure can solve the problems of agglomeration, adsorption and grain coarsening caused by the nanopowders as the starting materials in the conventional approach, which would be an alternative route to fabricate the fine-grained polycrystalline materials with the enhanced performances.

ANALYSIS OF THE MICROMORPHOLOGY AND STRUCTURE OF NANO Y-TZP MATERIALS SINTERED BY HOT_PRESSING

Sintering of Nanocrystalline ZrO_2(3Y) by Hot-Pressing

Sintering of Nanocrystalline ZrO2(3Y) by Hot-Pressing

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

Analysis of the Grain Growth of Nano Y-Tzp Materials

Influence of forming methods on the microstructure of 3Y-TZP specimens

Effects of Initial Density of Green Compact on Hot-Press Sintering and Superplastic Forming of Nano 3Y-TZP

Fabrication of nano Y-TZP by rapid hot-pressing and SPS

Hot-press Sintering and Superplastic Forming of Nano-Ceramics

Preparation Of Y-Tzp Nanoceramics By Gelcasting-Pressing And Pressureless Sintering

Microstructure and Thermal Deformation Behavior of Hot-Pressing Sintered Zr-6Al-0.1B Alloy

Study on Mechanical Properties of Hot Pressing Sintered Mullite-Zro2 Composites with Finite Element Method

Compacting and Sintering Behavior of Nano ZrO 2 Powders

Forming and Sintering of Y-TZP Nanoceramics

Fabrication of Nano Y-Tzp Materials by Superhigh Pressure Compaction

Preparation Of Y-Tzp Nanoceramics By Superhigh Pressure Compaction

[Influence of Compaction Pressure and Pre-Sintering Temperature on the Machinability of Zirconia Ceramic].

Microstructure and Mechanical Properties of ZrO2-2 Mol% Y2O3 Ceramics

Pressureless-sintering Behavior of Nanocrystalline ZrO2–Y2O3–Al2O3 System

Injection Molding Process and Microstructure of Ceramic Micro-Structured Part

Effect of holding time and pressure on the densification, microstructure and mechanical properties of hot pressed Al2O3-CA6-ZrO2/Ni multi-phase composites