Abstract:Constant current charging and discharging is widely used for nowadays commercial Lithium (Li) ion batteries (LIBs) in applications of portable electronic devices and electric vehicles. However, the main battery degradation mechanism during constant current cycling remains unclear. To unveil the aging mechanism during constant current cycling, in this work, electrochemical cycling, real-time temperature monitoring, and operando electrochemical impedance spectroscopy of a fresh and an aged battery have been carried out. The results of the incremental capacity analysis (ICA) analysis indicate that polarization is the main reason for the capacity fading during operation. Besides, post-mortem analysis of the electrodes reveals that the formation of solid-electrolyte interphase (SEI) and cathode-electrolyte interphase (CEI) is the leading cause of electrodes degradation. The interface formation and evolution over cycling (including thickening and chemical variation) leads to continuous loss of active materials. The presence of SEI and CEI also increases the impedance for charge transfer and transport and reduces the kinetics of electrochemical Li-ion redox on the electrodes. Moreover, the irreversible Li loss to Li plating and SEI formation has been quantified, which accounts for 16.8% of the total Li in the battery. This work provides a mechanistic understanding of the degradation mechanism of commercial LIBs and guides the rational design of the commercial battery and inspires the design of charging and discharging protocols toward enhanced cycling stability and prolonged cycle life.

Changes of some capacities and failure mode of Ni/MH batteries during cycling

Deterioration mechanism of LiNi0.8Co0.15Al0.05O2/graphite-SiOx power batteries under high temperature and discharge cycling conditions

Deterioration of Lithium Iron Phosphate/graphite Power Batteries under High-Rate Discharge Cycling

Investigation of LiNi1/3Co1/3Mn1/3O2 cathode particles after 300 discharge/charge cycling in a lithium-ion battery by analytical TEM

A Study of the Oxidation Determination of the Mm Hydrogen Storage Alloy and its Performance Degradation

Capacity Degradation Mechanisms in Nickel/Metal Hydride Batteries

Study of Early Cycling Deterioration of a Ni/MH Battery by Electrochemical Impedance Spectroscopy

Understanding the Mechanism of Capacity Increase During Early Cycling of Commercial NMC/graphite Lithium-Ion Batteries

Insights into the Deterioration Mechanism of Charging Ability during Calendar Aging and Cycling Aging of High-Voltage Co-Poor NCM Cathode-Graphite Full Battery

Electrochemical analysis of failed Ni-MH batteries

Cycling durability and degradation behavior of La–Mg–Ni–Co-type metal hydride electrodes

Coupled effects of charge–discharge cycles and rates on the mechanical behavior of electrodes in lithium–ion batteries

Research on Electrochemical Characteristics During Charge-Discharge Cycle of MH/Ni Battery

Unravelling and Quantifying the Aging Processes of Commercial Li(Ni0.5Co0.2Mn0.3)O2/Graphite Lithium-ion Battery under Constant Current Cycling

Investigation on Topographic, Electrochemical and Thermal Features of Aging Lithium-Ion Cells Induced by Overcharge/over-Discharge Cycling

Thermal behavior and failure mechanisms of 18650 lithium ion battery induced by overcharging cycling

Failure mechanisms of the Li(Ni 0.6 Co 0.2 Mn 0.2 )O 2 -Li 4 Ti 5 O 12 lithium-ion batteries in long-time high-rate cycle

Long-Term Cycling and Mechanisms of Cell Degradation of Single Crystal LiNi0.95Mn0.04Co0.01O2/Graphite Cells

Enhanced Long-Term Cycling Life of Ni-Rich NMC Cathodes in High-Voltage Lithium-Metal Batteries

Comprehensive Analysis on Aging Behavior and Safety Performance of LiNixCoyMnzO2/graphite Batteries after Slight Over-Discharge Cycle

In-depth understanding of the deterioration mechanism and modification engineering of high energy density Ni-rich layered lithium transition-metal oxide cathode for lithium-ion batteries