The Friction Behavior and Surface Topography of YBa2Cu3O7 Film in Ambient Environment

丁建宁,孟永钢,温诗铸

DOI: https://doi.org/10.3321/j.issn:1004-0595.2001.02.002

2001-01-01

Abstract:YBa2Cu3O7 film and polysilicon film were prepared over the oxidelayer of about 100 nm thick on Si substrate. The friction behavior of the films sliding against a sapphire ball or a steel ball in ambient environment was investigated with a ball-on-flat tribometer. The surface topography of the original film surfaces and worn film surfaces was examined by means of atomic force microscopy (AFM). As the results, the friction coefficient of YBa2Cu3O7 film is lower than that of polysilicon film when sliding against a sapphire ball. It is almost the same for the two films when sliding against a steel ball. The initial friction of YBa2Cu3O7 film in sliding against both sapphire ball and steel ball is much stable. However, the initial friction of polysilicon film in sliding against a sapphire ball fluctuates greatly during a cycle period. AFM observation of the original film surfaces and worn film surfaces indicates that super-conducting protrusions exist on the original YBa2Cu3O7 film surface. The protrusions are liable to remove during the friction process, thus the worn surface of YBa2Cu3O7 film becomes much smooth.