A Structural, Magnetostrictive and Mössbauer Study of Tb0.3Dy0.7(Fe0.9T0.1)1.95 Alloys
Zheng Xiaoping,Zhang Peifeng,Fan Duowang,Li Fashen,Hao Yuan
DOI: https://doi.org/10.1360/142005-170
2005-01-01
Abstract:The effect of IIIA metal and transition metalT substitution for Fe on crystal structure, magnetostriction and spontaneous magnetostriction, anisotropy and spin reorientation of a series of polycrystalline Tb0.3 Dy0.7 (Fe0.9 T 0.1)1.95 (T=Mn, Fe, Co, B, Al, Ga) alloys at room temperature were investigated systematically. It was found that the primary phase of the Tb0.3 Dy0.7 (Fe0.9 T 0.1)1.95 alloys is the MgCu2-type cubic Laves phase structure for different substitution. The magnetostrictionλ s decrases greatly for the substitution of IIIA metal, B, Al and Ga, but is saturated more easily for Al and Ga substitution, showing that the Al and Ga substitution is beneficial to a decrease in the magnetocrystalline anisotropy of Tb0.3 Dy0.7 (Fe0.9 T 0.1)1.95 alloys. However, the substitution of transition metal Mn and Co decreases slightly the magnetostrictionλ s . It was also found that the effect of different substitutions on the spontaneous magnetostrictionλ 111 is distinct. The analysis of the Mössbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry for Al and Ga substitution, namely spin reorientation, but it does not change evidently for B, Mn and Co substitution.