Intrinsic magnetostriction of Tb-Dy-Fe-Co alloy

Yue Cui,Chengbao Jiang,Huibin Xu

DOI: https://doi.org/10.3724/SP.J.1037.2010.00449

IF: 1.797

2011-01-01

ACTA METALLURGICA SINICA

Abstract:The distribution of Co, the intrinsic magnetism and magnetostriction of quaternary Tb-Dy-Fe-Co alloy were investigated. The SEM image showed the matrix (Laves phase) and the rare-earth (RE) rich phase in the annealed samples. The Co content (atomic fraction) in the RE rich phase was 21.18%, much higher than that in the matrix (9.36%). XRD patterns showed that Co partial substitution for Fe did not change the structure of MgCu 2-type cubic Laves phase, contributing to the giant magnetostriction. Curie temperature Tc was increased remarkably with Co addition, resulting in wider operating temperature. The magnetocrystalline anisotropy compensation by Co addition was beneficial to improving the magnetostriction in low field. The solidified orientation influences the testing of intrinsic magnetostriction. In order to ensure the accuracy in the measurements, the equiaxed Tb-Dy-Fe-Co samples were prepared. The saturated magnetostrictive constant λ s was tested. λ 111 and λ 100 were calculated by the cleavage of (440) diffraction peak of Laves phase. Compared with Terfenol-D alloy, λ 111 in the Co-doped sample decreased slightly, but λ 100 increased evidently and λ s almost remained unchanged. © Copyright.