Abstract:The as-cast Cu-12%Ag (mass fraction)alloy was pre-annealing treated either at the high temperature 700 degrees C for 2 h followed by 720 degrees C for 2 h or at the low temperature 450 degrees C for 10 h. The composite wires were prepared by drawing the annealed alloy at ambient temperature. The effect of the pre-annealing treatment on the properties of a Cu-Ag microcomposite with middle Ag content was investigated by observing the microstructure and measuring the tensile strength and electrical conductivity. The pre-annealing treatment at the high temperature will eliminate the dendritic segregation more completely in Cu matrix, reduces the volume fraction of eutectic colonies and induces the precipitation of coarse secondary particles, which can result in a low level of electron scattering at solute atoms and phase interfaces. The pre-annealing treatment at the low temperature will,eliminate the dendritic segregation partially, reserves some of non-equilibrium eutectic colonies and induces the precipitation of fine secondary particles, which can result in a high level of dispersion strengthening. There is higher tensile strength for the alloy pre-annealed at the low temperature and higher electrical conductivity for the alloy pre-annealed at the high temperature under the condition of certain draw deformation. In general, the pre-annealing treatment at the high temperature can obtain better matched relationship between strength and conductivity in the microcomposite compared with that at the low temperature.

Effects of in-situ composite Cu-Cr alloy cables by directional solidification on their synthetic properties

Directional Solidification Properties of the In-Situ Composite Cu-Cr Alloy

In-Situ Composite Cu-Cr Contact Cables with High Strength and High Conductivity

Effects of Cr addition on the microstructural, mechanical and electrical characteristics of Cu–6wt.%Ag microcomposite

Property and Thermal Stability of in Situ Composite Cu–Cr Alloy Contact Cable

Progress and Current Status in Research on Nanostructured Cu-Ag Microcomposites for Conductor Wires

Progress in Research on Nanoprecipitates in High-Strength Conductive Copper Alloys: a Review

EFFECT OF HEAVILY DRAWING ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Cr ALLOYS

Research and Development on Microstructure, Properties and Alloying of Cu-Ag Filamentary Composites

Effect of solid solution process on the structure and properties of Cu-Cr-Mg alloy in the aging state

Effects of pre-annealing process on microstructure and properties of the Cu-12%Ag composite wire

Effects of Ce additions on microstructure and properties of Cu-15Cr in situ composite

Microstructure and Property Evolution of an Al-Mg-Si Alloy Cable during the Production Process

Synergistic solid–liquid composite and rapid solidification preparation of aluminum-clad steel wires

Microstructure and Properties of High Strength and High Conductivity Cu-0.4Mg Alloy Processed by Upward Continuous Casting and Multi-pass Drawing

Effect of Iron Content on the Strength and Conductivity of Cu-Fe In Situ Composite

High electrical conductivity Al-Ag-Sc-Zr alloy with ultrafine grains processed by accumulative continuous extrusion

Microstructure and properties of Cu-Ag alloy prepared by continuously directional solidification

Simultaneous improvement on strength and conductivity of CrB 2 /Cu composites by inhomogeneous design

Design Strategy to Simultaneously Enhance Electrical Conductivity and Strength: Cold-Drawn Copper-Based Composite Wire with In-Situ Graphene

Simultaneous improvement of electrical conductivity and mechanical property of Cr doped Cu/CNTs composites