Abstract:Traditionally, structural wire is characterized by a homogeneous microstructure, where the average grain size in different parts of the wire is uniform. According to the classical Hall–Petch relationship, a homogeneous polycrystalline metal can be strengthened by decreasing the average grain size since an increase in the volume fraction of grain boundaries will further impede the motion of dislocations. However, a decrease in the grain size inevitably leads to a decrease in the ductility and deformability of the material due to limited dislocation mobility. Putting a gradient microstructure into the wire has promising potential for overcoming the compromise between strength and ductility. This is proposed a new combined technology in this paper in order to obtain a gradient microstructure. This technology consists of deforming the wire in a rotating equal-channel step die and subsequent traditional drawing. Deformation of copper wire with a diameter of 6.5 mm to a diameter of 5.0 mm was carried out in three passes at room temperature. As a result of such processing, a gradient microstructure with a surface nanostructured layer (grain size ~400 nm) with a gradual increase in grain size towards the center of the wire was obtained. As a result, the microhardness in the surface zone was 1150 MPa, 770 Mpa in the neutral zone, and 685 MPa in the central zone of the wire. Such a symmetrical spread of microhardness, observed over the entire cross-section of the rod, is a direct confirmation of the presence of a gradient microstructure in deformed materials. The strength characteristics of the wire were doubled: the tensile strength increased from 335 MPa to 675 MPa, and the yield strength from 230 MPa to 445 MPa. At the same time, the relative elongation decreased from 20% to 16%, and the relative contraction from 28% to 23%. Despite the fact that the ductility of copper is decreased after cyclic deformation, its values remain at a fairly high level. The validity of all results is confirmed by numerous experiments using a complex of traditional and modern research methods, which include optical, scanning, and transmission microscopy; determination of mechanical properties under tension; and measurement of hardness and electrical resistance. These methods allow reliable interpretation of the fine microstructure of the wire and provide information on its strength, plastic, and electrical properties.

Design Strategy to Simultaneously Enhance Electrical Conductivity and Strength: Cold-Drawn Copper-Based Composite Wire with In-Situ Graphene

In-situ graphene enhanced copper wire: A novel electrical material with simultaneously high electrical conductivity and high strength

Attaining Exceptional Electrical Conductivity in Cu-Fe Composite by Powder Rolling Strategy

Enhanced Tensile Properties And Fracture Reliability Of Cu-Based Amorphous Wires Via Pr-Doping

A high strength and high electrical conductivity graphene/Cu composite with good high-temperature stability

Superior electrical conductivity-strength combination of an in-situ fabricated La 2 O 3 -doped copper/graphene composite conductor

Progress and Current Status in Research on Nanostructured Cu-Ag Microcomposites for Conductor Wires

High strength and high electrical conductivity in copper reinforced with intra-/inter-granular graphene in-situ exfoliated from graphite

Copper coated graphene reinforced aluminum composites with enhanced mechanical strength and conductivity

Enhanced electrical conductivity and mechanical properties in thermally stable fine-grained copper wire

Strength-conductivity synergy in cold-drawn reduced graphene oxide (RGO)-aluminum composite wires for electrical applications

Investigation on the novel copper-based composite conductors synergistically improved by in-situ generated graphene and nanoparticles

Enhanced stress relaxation resistance and strength-electrical conductivity combination of graphene reinforced Cu-0.5La composite wire for high temperature applications

A high strength and high electrical conductivity copper based composite enhanced by graphene and Al2O3 nanoparticles

High strength and conductivity copper matrix composites reinforced by in-situ graphene through severe plastic deformation processes

Fabrication of a novel high-strength and high-conductivity copper-clad aluminum composite wire

In-situ generated graphene from wheat flour for enhancing mechanical and electrical properties of copper matrix composites

Relationships between mechanical strength and electrical conductivity for Cu–Ag filamentary microcomposites

Obtaining Symmetrical Gradient Structure in Copper Wire by Combined Processing

Fabrication and characterization of copper and copper alloys reinforced with graphene

Surface modification on copper particles toward graphene reinforced copper matrix composites for electrical engineering application