The Preparation of Fe3O4@Au Core-Shell Structure Materials and Its Application in Epoxidation of Styrene
Qing-xi CAO,Cong LU,Pei CHEN,Ya-jie GUO,Chang-nan LI,Guang-jian WANG
DOI: https://doi.org/10.3969/j.issn.2095-0691.2014.02.009
2014-01-01
Abstract:Mesoporous magnetic iron oxide (Fe3O4) nanospheres with average particle size of approximately 300 nm were synthesized using hydrothermal method at 200 ℃,using ferric chloride hexahydrate(FeCl3 · 6H2O)as iron source,ethylene glycol as the reducing agent,polyethylene glycol(PEG)as the surfactant. Then the Fe3O4 nanoparticles were chemically modified by using 3-aminopropyltriethoxysilane(APTES) as si-lylation reagent. Subsequently,the well-defined mesoporous Fe3O4(core)@Au(shell) structures nanospheres with high monodispersity were obtained under ultrasonic at room temperature with sodium citrate adding drop-wise as the reducing agent for reducing Au3+ to Au0. The morphology and crystal structure of the as-prepared nanocomposites were characterized by scanning electronic microscopy(SEM),N2 adsorption-desorption iso-therms,X-ray powder diffraction(XRD)patterns,Fourier transform infrared(FT-IR)spectroscopy et al. The re-sults showed that the surface area of Fe3O4 nanoparticle and the nanospheres diameter prepared us-ing the method were 95.56m2/g and 5.67 nm,respectively. Besides,the spherical central Fe3O4 cores were coated by a uniform Au layer. Furthermore,the nanocomposites has a good effect on selectivity photocatalytic epoxidation.