A Magnetic and Moessbauer Spectral Study of Core/Shell Structured Fe/Au Nanoparticles

Sung-Jin Cho,Ahmed M. Shahin,Gary J. Long,Joseph E. Davies,Kai Liu,Fernande Grandjean,Susan M. Kauzlarich

DOI: https://doi.org/10.1021/cm0522073

2005-12-17

Abstract:Fe/Au nanoparticles have been chemically synthesized through a reverse micelle reaction and investigated by both conventional and synchrotron based x-ray diffraction and by magnetic and Moessbauer spectral studies. The powder x-ray diffraction patterns reveal both the presence of crystalline alpha-iron and gold and the absence of any crystalline iron oxides or other crystalline products. First-order reversal curves, along with the major hysteresis loops of the Fe/Au nanoparticles have been measured as a function of time in order to investigate the evolution of their magnetic properties. The iron-57 Moessbauer spectra of both uncoated iron nanoparticles and the Fe/Au nanoparticles have been measured at 78 and 295 K and indicate that two major iron containing components are present, namely the expected alpha-iron and the unexpected amorphous Fe1-xBx alloy; several poorly crystallized ordered iron(III) oxide components as well as paramagnetic iron(II) and iron(III) components are also observed. These results indicate that the Fe-core/Au-shell nanoparticles synthesized through reverse micelles are far more complex that had been believed.

Materials Science

What problem does this paper attempt to address?

The problems that this paper attempts to solve are related to the composition and oxidation of Fe/Au core - shell structure nanoparticles. Specifically:

1. **Complexity of Core - Shell Structure Nanoparticles**: Although the X - ray diffraction (XRD) results show that these nanoparticles are mainly composed of α - iron and gold, Mössbauer spectroscopy studies have revealed more complex components. Besides the expected α - iron phase, there are also amorphous Fe\(_{1 - x}\)B\(_x\) alloys and several iron oxide species with poor crystallinity.

2. **Oxidation Problem of the Iron Core**: The researchers are particularly concerned about whether the iron core will be oxidized after synthesis, because this directly affects the magnetic properties of the nanoparticles. Although the gold shell was initially thought to protect the iron core from oxidation, the experimental results show that this protection is not completely effective, and the iron core will still gradually oxidize, especially when exposed to air.

3. **Evolution of Magnetic Properties**: By measuring the first - order reversal curves (FORC) and hysteresis loops at different time points, the researchers attempt to understand how the magnetic properties of these nanoparticles change over time. The experimental results show that as the oxidation process occurs, both the coercivity and the saturation magnetization of the nanoparticles decrease.

4. **Composition Analysis and Characterization**: Through a variety of technical means (such as XRD, TEM, Mössbauer spectroscopy, etc.), the researchers have carried out detailed composition analysis and structural characterization of Fe/Au core - shell structure nanoparticles to verify their composition and explore their formation mechanism.

In summary, this paper aims to deeply understand the real composition of Fe/Au core - shell structure nanoparticles and the oxidation processes that may occur after synthesis, and to explore the influence of these factors on their magnetic properties.