Synthesis, structure and magnetic properties of Fe@Pt core-shell nanoparticles

Kelly L. Pisane,Sobhit K. Singh,Mohindar S. Seehra

DOI: https://doi.org/10.1063/1.4908304

2015-02-03

Abstract:Structural and magnetic properties of Fe@Pt core-shell nanostructure prepared by a sequential reduction process are reported. Transmission electron microscopy (TEM) shows nearly spherical particles fitting a lognormal size distribution with $D$$_o$= 3.0 nm and distribution width $\lambda$$_D$= 0.31. In x-ray diffraction, Bragg lines due to Pt shell only are clearly identified with line-widths yielding crystallite size =3.1 nm. Measurements of magnetization $M$ vs. $T$ (2 K - 350 K) in magnetic fields up to 90 kOe show a blocking temperature $T$$_B$ = 13 K below which hysteresis loops are observed with coercivity $H$$_C$ increasing with decreasing $T$ reaching $H$$_C$ = 750 Oe at 2 K. Temperature dependence of the ac susceptibilities at frequencies $f$$_m$ = 10 Hz to 5 kHz is measured to determine the change in $T$$_B$ with $f$$_m$ using Vogel-Fulcher law. This analysis shows the presence of significant interparticle interaction, the Néel-Brown relaxation frequency $f$$_o$ = 5.3 x 10$^{10}$ Hz and anisotropy constant $K$$_a$ =3.6 x10$^6$ ergs/cm$^3$. A fit of the $M$ vs. $H$ data up to $H$ = 90 kOe for $T$ $>$ $T$$_B$ to the modified Langevin function taking particle size distribution into account yields magnetic moment per particle consistent with the proposed core-shell structure; Fe core of 2.2 nm diameter and Pt shell of 0.4 nm thickness.

Mesoscale and Nanoscale Physics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the study of the synthesis, structure and magnetic properties of Fe@Pt core - shell nanoparticles (NPs). Specifically, the research aims to:

1. **Synthesize Fe@Pt core - shell nanoparticles**: Synthesize Fe@Pt core - shell nanoparticles with specific sizes and structures through a sequential reduction process. This involves selecting appropriate precursors and reaction conditions to ensure the formation and stability of the nanoparticles.

2. **Characterize the structure of nanoparticles**: Use techniques such as transmission electron microscopy (TEM) and X - ray diffraction (XRD) to determine the morphology, size distribution and crystal structure of the nanoparticles. The study found that the nanoparticles are approximately spherical, with an average diameter of 3.0 nm, and only the Bragg lines of the Pt shell were observed, indicating that the Fe core may be partially blocked by the Pt shell or be in an amorphous state.

3. **Study the magnetic properties of nanoparticles**: Explore the magnetic behavior of Fe@Pt core - shell nanoparticles by measuring the change of magnetization with temperature and magnetic field. The study found that these nanoparticles exhibit significant hysteresis at low temperatures, with a blocking temperature \(T_B = 13\) K, and as the temperature decreases, the coercive force \(H_C\) increases, reaching 750 Oe at 2 K.

4. **Analyze magnetic data and explain its physical mechanism**: Use the modified Langevin function and log - normal distribution to fit the relationship between magnetization and magnetic field, calculate the magnetic moment of each nanoparticle, and evaluate the inter - particle interactions. The research results show that there are significant inter - particle interactions (IPI), and the magnetic anisotropy constant \(K_a\) is an order of magnitude higher than that of bulk iron.

In summary, this paper mainly focuses on how to synthesize and characterize Fe@Pt core - shell nanoparticles by experimental means, and deeply explores their unique magnetic properties and the physical mechanisms behind them. This research is of great significance for the development of new magnetic materials and the understanding of magnetic behavior at the nanoscale.