Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Studies on the Synthesis and Physicochemical Property of Mesoporous Titanosilicate with High Titanium Content

Novel Synthesis of Ordered Mcm-41 Titanosilicates with Very High Titanium Content Via Ultrasound Radiation

Synthesis of titanium silicalite-1 (TS-1) zeolite with high content of Ti by a dry gel conversion method using amorphous TiO2–SiO2 composite with highly dispersed Ti species

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Synthesis of Ti-containing mesoporous silicates from inorganic titanium sources

Synthesis, Characterization and Catalytic Performance of Ti-Containing Mesoporous Molecular Sieves Assembled from Titanosilicate Precursors

Ordered Mesoporous Titanosilicates with Better Catalytically Active Titanium Sites Assembled from Preformed Titanosilicate Precursors with Zeolite Building Units in Alkaline Media

Synthesis of easily shaped ordered mesoporous titanium-containing silica

Studies on the synthesis of titanium silicalite, TS-1

Synthesis of Nanoporous Titanosilicates and Their Structural Characterization by Physical Nitrogen Adsorption

Incorporation of Titanium into Mesoporous Silica Molecular Sieve SBA-15

Synthesis, Characterization, and Catalytic Activity of Mesostructured Titanosilicates Assembled from Polymer Surfactants with Preformed Titanosilicate Precursors in Strongly Acidic Media

Epoxidation of Propylene with Dilute H 2 O 2 over Titanium Silicalite Containing Trace Aluminum

Direct Synthesis and Structural Characteristics of Titanium Dioxide/Mesoporous SBA-15 Materials

Direct Synthesis and Characterization of Titanium-Substituted Mesoporous Molecular Sieve Sba-15

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

The silanization process for the hydrothermal synthesis of hierarchical titanium silicalite-1

The synthesis and characterization of titanium silicalite-1

The Study of Ti Ions Post-synthesis in Mesoporous MCM-41

Silica–Titania mixed Oxides: Si–O–Ti Connectivity, Coordination of Titanium, and Surface Acidic Properties

Synthesis and Characterization of Hierarchical Titania-Silica Monolith