Structure, Magnetic Property and GMR Effects of Co-C Granular Thin Films
Ma Lei,Zhongwu Liu,Zeng Dechang,Xiaping Zhong,Gang Cheng
DOI: https://doi.org/10.3969/j.issn.1002-185x.2013.08.024
2013-01-01
Rare Metal Materials and Engineering
Abstract:CoxC100x (x=2.5 similar to 50, at%) granular films were prepared on n-Si (100) substrates by d.c. magnetron sputtering, and the structure, morphology, magnetic properties and giant magnetoresistive (GMR) effects of the films were investigated. The as-deposited Co-C granular films are amorphous, which have fairly smooth and flat surface. With the increase of annealing temperature, the Co (002) peak of the Co-C films is obtained at 300 degrees C, but cracks appear in the films after annealing at 500 degrees C for 0.5 h. The X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy results show that the as-deposited Co-C films are diamond like carbon (DLC) films, and the doping of Co existing in atomic state does not enhance the graphitization of carbon film. The nano-sized amorphous Co particles are homogeneously encapsulated in the amorphous cross-linked carbon matrix, thereby forming a good metal/insulator system. Saturation magnetization (M-s) and the coercivity (H-c) of CoxC100-x, films are dependent on Co concentration and the amount of crystallized Co. The as-deposited CO2.5C97.5 granular films exhibit a novel positive GMR effect, up to 36%. The GMR effects of the Co-C granular films follow a variable transport channel mechanism.