Abstract:In order to achieve desired mechanical properties of alloys by manipulating grain boundaries (GBs) via solute decoration, it is of great significance to understand the underlying mechanisms of microstructural evolution and plastic deformation. In this work, nanocrystalline (NC) Cu-W alloyed films with W concentrations spanning from 0 to 40 at% were prepared by using magnetron sputtering. Thermal stability (within the temperature range of 200 °C-600 °C) and hardness of the films were investigated by using the x-ray diffraction, transmission electron microscope (TEM) and nanoindentation, respectively. The NC pure Cu film exhibited substantial grain growth upon all annealing temperatures. The Cu-W alloyed films, however, displayed distinct microstructural evolution that depended not only on the W concentration but also on the annealing temperature. At a low temperature of 200 °C, all the Cu-W alloyed films were highly stable, with unconspicuous change in grain sizes. At high temperatures of 400 °C and 600 °C, the microstructural evolution was greatly controlled by the W concentrations. The Cu-W films with low W concentration manifested abnormal grain growth (AGG), while the ones with high W concentrations showed phase separation. TEM observations unveiled that the AGG in the Cu-W alloyed thin films was rationalized by GB migration. Nanoindentation results showed that, although the hardness of both the as-deposited and annealed Cu-W alloyed thin films monotonically increased with W concentrations, a transition from annealing hardening to annealing softening was interestingly observed at the critical W addition of ∼25 at%. It was further revealed that an enhanced GB segregation associated with detwinning was responsible for the annealing hardening, while a reduced solid solution hardening for the annealing softening.

The Preparation and Morphological Investigation of Nano-scale Cu-C60 Codeposited Granular Films

In Situ Direct-Current Conductance Investigation Of Cu/C-60 Nano-Scale Granular Films

Preparation and Structural Characterization of Nanostructured Coag Granular Films

Structure and Properties of Electrocodeposited Cu-Al2o3 Nanocomposite Thin Films

Characteristic of Interface Effect in Cu–C60 Granular Films

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

Formation of (110) oriented layered silver nano-crystallites

Synthesis and Characterization of Ag–C60 Nanostructure Film

Experimental study of scaling properties and roughing mechanisms in C 60 -Ag thin films

Synthesis and Characterization of Metal-C-60 Nanostructured Films

Size-Dependent Magnetic Properties of Ni/C-60 Granular Films

The Surface Condition Effect of Cu2O Flower/grass-Like Nanoarchitectures Grown on Cu Foil and Cu Film

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Microstructural investigation of as-deposited Co-Ag nano-granular films

Studies of C-60 Films Deposited Using Ionized Cluster Beam Deposition Technique

Microstructural Investigation of As-deposited Nano-Granular CoAg Films by High Resolution Electron Microscopy

Cu–C60 interaction and nano-composite structures

Structural and Electronic Studies of C60 Films Deposited Using a New Technique of Neutral Cluster Beam Deposition

Synthesis, characterization and properties of C 60 nanocrystals, nanowires and hierarchical nanostructures

Investigation on the Interfacial Stability of Multilayered Cu–W Films at Elevated Deposition Temperatures During Co-Sputtering

THE PREPARATION OF ORGANIC AND INORGANIC FILM ON ALIGNED CARBON NANOTUBES