Abstract:Selective laser sintering (SLS) combined with reaction melt infiltration was used to fabricate Si–SiC ceramic matrix composites, and the effects of different concentrations of phenolic resin (PF) on the properties of the SLS green body and carbonized and final Si–SiC samples were investigated. The results showed that the impregnation with PF can increase the bulk density, reduce the porosity of the samples at all stages, and improve the mechanical properties of the reactive bonded samples. The degree of densification and mechanical properties of the sample gradually enhanced with an increase in PF concentration. The main phases of the Si–SiC composites were free Si, α-SiC, β-SiC, plus an extremely small amount of Al–Si alloy, and the SiC and the Si phase contents increased and decreased, respectively, as the concentration of PF increased when measured using Rietveld refinement and image analysis software. The macroscopic properties of the samples improved greatly after precursor infiltration pyrolysis (PIP) treatment with 66.7%vol PF-ethanol solution twice. According to the crystal nucleation-growth theory, it was inferred that the infiltrated PF could provide a certain amount of pyrolytic carbon in the carbonized specimen. During the reaction bonded process, the carbon formed by carbonization pyrolysis first dissolves into the molten Si and reaches saturation. With the further dissolution of carbon, [C] and [Si] in the liquid phase contact each other to form β-SiC nuclei, the nuclei that precipitate at the pore wall position and gradually form a continuous interfacial layer of β-SiC. The β-SiC layer prevents the liquid Si from direct contact with C inside the prefabricated body, therefore, further reactants diffuse through the layer. Finally, the fine crystalline β-SiC grains were fabricated inside the specimen.

Microstructures of the Si-SiC Composites Made by the Reaction Sintering of Liquid Silicon and Carbon Felt

Study of Rapid Fabrication and Microstructure of C/C-SiC Composites

Microstructure Evolution and Reaction Mechanism of Microporous Carbon Derived SiC Ceramic

SiC Micro-Threads Prepared Within the Carbon Fiber Felt

Effect of impregnated phenolic resin on the properties of Si–SiC ceramic matrix composites fabricated by SLS-RMI

Microstructure and Properties of Reaction-Formed SiC Ceramic Derived from Mesocarbon Microbeads

Microstructural characterization of sintered MoSi2/SiCp composites

Fabrication and Properties of Reaction-Formed SiC by Infiltrating Molten Si into Mesocarbon Microbeads-Based Carbon Preform

Microstructural Characterization of Sintered MoSi<sub>2</sub>/SiC<sub>P</sub> Composites

Characterization of the Microstructure of Three‐Dimensional‐Needled Carbon/Silicon Carbide Composites

Microstructure and Mechanical Properties of Cf/SiC Composites with Dispersed C-SiC Interphase Prepared by Chemical Vapor Infiltration

Preparation of SiC/C Composites by Si Gaseous Infiltration

The Melt Structural Characteristics Concerning the Interfacial Reaction in SiC(p)/Al Composites

Preparation and microstructure analysis of C/C-SiC-Si composite

Studies of microstructure and mechanical properties of SiC/B4C composites based on reaction sintering

Reactions Mechanism and Mechanical Properties of a SiCf/SiC Joint Affected by Cu/Ni/Ti Elements and Inhomogeneous Composites

Fabrication, Microstructure, and Properties of SiC/Al 4 SiC 4 Multiphase Ceramics Via an In-Situ Formed Liquid Phase Sintering

Microstructure and mechanical properties of short-carbon-fiber/Ti3SiC2 composites

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

Microstructure and Mechanical Properties of Sicp/Mg-Zn-Ca Composites Fabricated by Stir Casting

Microstructure and Thermal Conduction Property of SiCp/Al- Si Composite with High Reinforcement Content