Abstract:Polycarbosilane (PCS) serves as a crucial precursor for silicon carbide (SiC) fibers and ceramics. However, both of the precursor and the resulting SiC ceramics are carbon-rich, which is often viewed as detrimental to their relevant high-temperature properties. In this work, PCS is modified using nanosized Si particles to improve SiC grain growth and reduce carbon content in the resulting SiC ceramics, and the structural evolution during the polymer–ceramic conversion process has been meticulously investigated. The findings reveal that the incorporation of nano-Si into PCS raises its actual ceramic yield and accelerates the organic-inorganic conversion process. This is attributed to the formation of a more crosslinked structure at 200 °C–350 °C, resulting from the reaction between the Si–OH groups in nanosized Si and the Si–H and Si–CH3 groups in PCS. The carbothermic reaction between nano-Si and the free carbon starts at approximately 1200 °C at the periphery of nanosized Si particles, and is accomplished at around 1400 °C. This leads to the formation of large-sized reactive β-SiC. Simultaneously, PCS-derived β-SiC with smaller sizes is also formed at 1300 °C–1400 °C. At 1600 °C–1800 °C, the growth of the reactive and the derived β-SiC in nano-Si-modified PCS is both accelerated due to a substantial decrease in the free carbon content. Consequently, the grain size of β-SiC is much larger than that of unmodified PCS. Additionally, the residual amorphous free carbon transforms into nanocrystalline carbon at around 1400 °C and evolves into graphite carbon at 1600 °C–1800 °C, which exhibits a more ordered structure with larger size compared to that in unmodified PCS.

Melt Spun of Continuous Polycarbosilane Fibers

Preparation of SiC ceramic fiber from a photosensitive polycarbosilane

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

Synthesis of Polytitanocarbosilane and Preparation of Si–C–Ti–B Fibers

Synthesis and characteristics of polycarbomethylsilane via a one-pot approach

Fabrication of SiC ultrafine fiber with low oxygen content by electrospinning, thermal curing and pyrolysis of cyano-polycarbosilane

Fabrication of Homogeneous Mullite-Based Fiber Porous Ceramics with High Strength and Porosity

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Flexible and thermally stable SiC fiber mats derived from electrospun boron-doped polyaluminocarbosilane precursors

Fine-diameter Si–B–C–N ceramic fibers enabled by polyborosilazanes with N–methyl pendant group

Additive manufacturing of high mechanical strength continuous Cf/SiC composites using a 3D extrusion technique and polycarbosilane‐coated carbon fibers

Polycrystalline Nanograin Formation in Uniform-Sized Silicon Carbide Fibers Derived from Aluminum-Containing Polycarbosilane

Effect of Impurities Control on the Crystallization and Densification of Polymer-Derived SiC Fibers

Additive manufacturing of continuous carbon fiber-reinforced silicon carbide composite by fused filament fabrication and precursor infiltration pyrolysis

Conversion of silicon carbide fibers to continuous graphene fibers by vacuum annealing

Superparamagnetic Silicon Carbonitride Ceramic Fibers Through In Situ Generation of Iron Silicide Nanoparticles During Pyrolysis of an Iron-Modified Polysilazane

Polyacrylonitrile Fibers with a Gradient Silica Distribution as Precursors of Carbon-Silicon-Carbide Fibers

Fabrication of continuous SiOC ceramic fibers by polyethylene oxide assisted sol-gel method

Influence of polycarbosilane composition on the properties of SiC/SiC composite fabricated by precursor infiltration and pyrolysis process

Poly(Methyl Methacrylate)/Silica Nanocomposite Fibers by Electrospinning

Polymethylsilane As A Precursor to High-Purity Silicon-Carbide