Abstract:To resolve the serious breakage and leakage problems for the cast iron water mains buried in the early years in the water-supply system, pipe stresses were firstly calculated based on the pipe soil interaction model, and the failure prediction model for the cast iron pipe was developed, based on the corrosion model, the residual strength evaluation method and the failure criterion. Monte Carlo (MC) simulations were used to perform the probabilistic analysis, and the influence parameters analysis was given. Results show that pipes in large diameters are often broken because of circumferential stresses, and pipes in small diameters are prone to fail due to longitudinal stresses. The influence on the failure probability is large due to soil bedding lost induced by the breakage or uneven settlement when the corrosion depth reaches a certain depth. The corrosion model parameters, unsupported bedding length, and the residual strength parameters have large influence on the distribution of the safety factors for the cast iron pipe. The corrosion is one of the most important factors leading to the pipe failure. Reducing corrosion pit depth growth by using corrosion control technique can be the most effective way to decelerate the breakage growth rate and prolong the service life.

A mathematical model for predicting shrinkage defect of ductile iron castings

Simulation Analysis of Thermal Stress During Casting Process of Large-Sized Alloy Steel Ingot

Failure Prediction Model and Influence Parameter Analysis of Buried Cast Iron Water Mains

Numerical simulation of shrinkage cavity formation in spheroidal graphite iron castings based on micro modeling

PREDICTION OF SHRINKAGE CAVITY AND POROSITY IN GRAY CAST IRON DURING SOLIDIFICATION

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Continuous Casting Mould for Square Steel Billet Optimised by Solidification Shrinkage Simulation

A Method on Computer Prediction of Shrinkage Defect of Ductile Iron Casting by EPC Process

Progress in Solidification Modeling of Cast Iron in China

Criteria for Prediction of Shrinkage Cavities and Porosity in Castings

A Mathematical Model for Simulating the Microporosity of Squeeze Casting of Aluminum Alloy

Study on numerical simulation of mold-filling and solidification processes of shaped casting

Study and Application of Mold Filling Simulation of Shaped Castings

A Thermomechanical Finite Element Model for Simulating the Solidification Process of Squeeze Casting

Study of solidification shrinkage of ductile iron in dry sand molds

Progress on Numerical Simulation of Mold Filling and Solidification Processes of Shaped Castings

Modeling of Shrinkage Cavity Formation and Proces s Improvement of S.G.Iron Hub Casting

Mathematical Model of Fluid Flow and Solidification in Mold Region of Continuous Slab Casting

Experimental study and numerical simulation of solidification in large steel ingot

Shrinkage Behaviour of Spheroidal Graphite Cast Iron in Green and Dry Sand Molds for the Benchmarking of Solidification Simulation

Numerical simulation of microporosity evolution of aluminum alloy castings