Abstract:The FeAl/Al 2 O 3 composites were fabricated by hot-pressing process in this research. The Fe-Al intermetallics compounds powders were fabricated by mechanical alloying and heat treatment. The FeAl powders and Al 2 O 3 powders were mixed and the FeAl/Al 2 O 3 composite powders were prepared. The FeAl/Al 2 O 3 composites bulks were fabricated by hot-pressing process at 1300°C for 2h under the pressure of 35MPa. The phase composition and microstructure of the FeAl intermetallics compounds powders produced by mechanical alloying and heat treatment were investigated. The phase composition and microstructure of the FeAl/Al 2 O 3 composites produced by hot-pressing process were investigated. The XRD patterns results showed that the Fe-Al intermetallics compounds powders were fabricated by mechanical alloying for 60h. The FeAl intermetallics compounds powders were fabricated by heat treatment at 800°C, 900°C and 1000°C. The microstructure showed that the mean particles size of the FeAl intermetallics compounds powders produced by mechanical alloying and heat treatment was rather fine and about 4-5μm. The XRD patterns results showed that there existed FeAl phase and Al 2 O 3 phase in sintered composites. The FeAl/Al 2 O 3 composites bulks exhibited the homogenous and compact microstructure. The mean particles size of FeAl was about 4-5μm and the mean particles size of Al 2 O 3 was about 4-5μm. The microstructure of the FeAl/Al 2 O 3 composites became more homogenous and compact with the increase of FeAl content.

Microstructure and mechanical properties of Fe-Al-intermetallic compounds/Al2O3 composites manufactured by hot pressing

Effect of Sintering Temperature on Microstructure and Mechanical Properties of Hot-Pressed Fe/FeAl2O4 Composite

Microstructure and Mechanical Properties of FeAl Intermetallics Prepared by Mechanical Alloying and Hot-Pressing

Investigation of Phase Composition and Microstructure of the FeAl/Al<sub>2</sub>O<sub>3</sub> Composites Fabricated by Mechanical Alloying and Hot-Pressing Process

Fabrication and Properties of Fe3Al Nano-Particle Toughening Al2O3 Matrix Composites

Preparation and mechanical properties of Fe3Al/Al2O3 nano-/micro-composite

Microstructure and mechanical properties of Al2O 3/TiAl in situ composites doped with Fe2O3

Microstructure and mechanical properties of Ti3(Al,Ga)C2/Al2O3 composites prepared by in situ reactive hot pressing

Microstructures and Mechanical Properties of in Situ Al 2 O 3 /Al-Si Composites Fabricated by Reaction Hot Pressing

Microstructure and Mechanical Properties of in Situ Tial/Ti2alc Composites Prepared by Reactive Hot Pressing

Microstructures and Mechanical Properties of Fe–28Al–5Cr/TiC Composites Produced by Hot-Pressing Sintering

Synthesis, Microstructure and Mechanical Properties of Cr2AlC/Al2O3 in Situ Composites by Reactive Hot Pressing

Reactive hot pressing and mechanical properties of TiAl3/Ti3AlC2/Al2O3 in situ composite

Fabrication and mechanical properties of FeAl/TiC composites

Study on FeAl/TiC composites fabricated by reactive hot-pressing

Effect of sintering temperature on microstructure and mechanical properties of Al2O3/TiAl in situ composites

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

Microstructure and Mechanical Properties of Ti2AlC Particle and In-Situ TiAl3 Reinforced Pure Al Composites

Mechanical Properties and Microstructure of Fe40al/Tic Composites with Low Content of Intermetallic

Preparation of FeAl/TiC Composites by Reactive Hot Pressing

Mechanical properties of hot-pressed Al2O3/SiC composites