Fracture toughness of hot-pressed Al67Mn8Ti24Nb1 intermetallics consolidated with metastable powder

Yunayi Fu,Gengxiang Hu,Wangyue Yang,Zuqing Sun
2000-01-01
Abstract:During the high energy ball milling process, the DO22 second phase in the cast Al67Mn8Ti24Nb1 alloy gradually dissolves into the L12 matrix and the degree of ordering of the L12 matrix will decrease. After 10 h milling, the second phase was completely dissolved and the matrix changed into a weakly ordered fcc structure. The MM'ed metastable powder was consolidated by vacuum hot pressing. The microstructure of the hot-pressed Al67Mn8Ti24Nb1 alloy consists of the L12 matrix and DO22 Al3(Ti, Nb) second phase again. The grain size of the hot-pressed alloy is much smaller than that of the cast alloy. The very fine second phase disperses around the grains and inside the matrix. The room-temperature compressive strength and ductility of the hot-pressed PM alloy increases significantly than that of the cast alloy, and the fracture toughness also improves.