FRACTURE TOUGHNESS OF HOT-PRESSED Al67Mn8Ti24Nb1 INTERMETALLICS CONSOLIDATED WITH METASTABLE POWER

FU Yunyi,HU Gengxiang,YANG Wangyue,SUN Zuqing
DOI: https://doi.org/10.3321/j.issn:1005-3093.2000.04.017
2000-01-01
Abstract:During the high energy ball milling process, the DO22 second phase in the cast A167Mn8Ti24Nb1 alloy gradually dissolved into the L12 matrix and the degree of ordering of the L12 matrix will decrease. After 10h milling, the second phase was completely dissolved and the matrix changed into a weakly ordered fcc structure. The MM'ed metastable powder was consolidated by vacuum hot pressing. The microstructure of the hot-pressed Al67 Mn8Ti24 Nb1 alloy consists of the L12 matrix and DO22 A13(Ti, Nb) second phase again. The grain size of the hot-pressed alloy is much smaller than that of the cast alloy. The very fine second phase dispersed around the grains and inside the matrix. The room-temperature compressive strength and ductility of the hot-pressed PM alloy increased significantly than that of the cast alloy, and the fracture toughness also improved.
What problem does this paper attempt to address?