Abstract:This paper investigates the effect of the element La on plasma nitriding of the CoCrCuFeNi high-entropy alloy (HEA) at 440 °C for 8, 16, and 24 h. The phase composition, morphology, and hardness distribution of the nitrided layer are characterized using XRD, optical microscopy, and a microhardness tester. Furthermore, the corrosion resistance is tested using an electrochemical workstation. The study evaluated the friction and wear performance using a testing machine and scanning electron microscope. The thickness of the effective hardening layer after 16 h of treatment with La was similar to that after 24 h of treatment without La. The addition of La significantly increased the growth rate constant of the effective hardening layer from 0.53 × 10−14 m2/s to 0.72 × 10−14 m2/s. In addition, an expanded FCC phase with greater interplanar spacing can be formed on the surface of the sample by introducing La into the plasma nitriding process. This indicates that the expanded FCC phase, with a higher concentration of interstitial nitrogen atoms, can effectively improve the corrosion resistance of the specimen surface. The corrosion rate of the specimen surface was reduced by 27.5% and the wear rate was reduced by 41.7% after 16 h of treatment with the addition of La compared to 24 h of nitriding without the addition of La. It has been shown that the addition of La to the plasma nitriding process results in a higher quality nitrided layer in a shorter time and also demonstrates that La has the potential to optimize the surface properties of plasma nitrided HEAs.

DIFFUSION OF La IN PLASMA RE ION NITRIDED SURFACE LAYER AND ITS EFFECT ON NITROGEN CONCENTRATION PROFILES AND PHASE STRUCTURES

Acceleration of Plasma Nitriding at 550 °C with Rare Earth on the Surface of 38CrMoAl Steel

Low-Temperature Plasma Nitriding of 3Cr13 Steel Accelerated by Rare-Earth Block

Improvement in Surface Properties of M50NiL Steel by Plasma Nitriding with Rare Earth Addition

Effect of rare earth addition on microstructure and corrosion behavior of plasma nitrocarburized M50NiL steel

The Effect of La on the Surface Properties of Plasma Nitrided CoCrCuFeNi High-Entropy Alloys at 440 Degrees Celsius

Analysis Of Valence Electron Structure In Compound Layer Of Steel 42crmo Plasma Nitrided With Rare Earth Addition

Microstructure and mechanical properties of M50NiL steel plasma nitrocarburized with and without rare earths addition

Diffusion and Micro-Alloying Mechanism of Rare Earth(re) and Carbon/nitrogen Atoms Permeated into Surface Layer of Steel During RE-carburizing,-nitriding And-Nitrocarburizing

An effective and innovative application of rare-earth plasma nitriding on high entropy alloy CoCrCuFeNi

The diffusion behavior and surface properties of catalytic nitriding with LaFeO 3 film prepared by the sol-gel method

Nurmerical simulation of nitrogen concentration profile in 42CrMo steel during plasma nitriding

Effect of Rare Earth Element Lanthanum on the Microstructure and Erosion Resistance of Nitrided Layer on 38CrMoAl Steel

Characterisation of Rare Earth Assisted Plasma Carbonitrided TiNi Alloys

First-principles analysis on the role of rare-earth doping in affecting nitrogen adsorption and diffusion at Fe surface towards clarified catalytic diffusion mechanism in nitriding

Numerical Prediction Of Compound Layer Growth Of Steel En40b During Plasma Nitriding

Study on depth-related microstructure and wear property of rare earth nitrocarburized layer of M50NiL steel

Phase constitution control of plasma nitrided layer and its effect on wear behavior under different loads

Effect of Rare Earth Elements on the Erosion Resistance of Nitrided 40cr Steel