Low-Temperature Plasma Nitriding of 3Cr13 Steel Accelerated by Rare-Earth Block
Yuan You,Rui Li,Mufu Yan,Jihong Yan,Hongtao Chen,Chaohui Wang,Dongjing Liu,Lin Hong,Tingjie Han
DOI: https://doi.org/10.3390/coatings11091050
IF: 3.236
2021-08-31
Coatings
Abstract:The plasma nitriding of 3Cr13 steel occurred at 450 °C for 4, 8 and 12 h in NH3 with and without rare earth (RE). The nitrided layers were characterized using an OM, SEM, TEM, XRD, XPS, microhardness tester and electrochemical workstation. The modified layer, with and without La, are composed of a compound layer and diffusion layer from surface to core. After the addition of La during nitriding, the maximum increase of layer thickness, mass gain and average microhardness was 15.6%, 35.8% and 212.50HV0.05, respectively. With the increase of the proportion of ε-Fe2-3N, the passivation zone of the corrosion resistance curve increases from 2.436 to 3.969 V, the corrosion current density decreases, the corrosion potential and pitting potential both increase, and, consequently, the corrosion resistance is significantly improved. Most of the surface microstructures of the nitrided layer was refined by the addition of La. The presence of La reduces the N content in the modified layer, which accelerates the diffusion of N atoms and, thus, accelerates the nitriding process.
materials science, multidisciplinary,physics, applied, coatings & films