Phase constitution control of plasma nitrided layer and its effect on wear behavior under different loads

Tiantian Peng,Yao Chen,Xiliang Liu,Meihong Wu,Yangyang Lu,Jing Hu

DOI: https://doi.org/10.1016/j.surfcoat.2020.126403

IF: 4.865

2020-12-01

Surface and Coatings Technology

Abstract:<p>Plasma nitriding was conducted at different nitrogen ratio under the same nitriding condition of 510 °C and 4 h for AISI 4340 steel in this study, the phase constitution of nitrided layer was controlled by adjusting nitrogen ratio and its effect on wear behavior under different loads was investigated. The results showed that the phase constitution of plasma nitrided layer could be precisely controlled by adjusting nitrogen ratio, a compound-free nitrided layer, single γ′ phase and ε + γ′ dual-phase compound layer was obtained at nitrogen ratio of 15%, 20% and 25%, respectively. And it was found that the hardness increased gradually for compound-free nitrided layer, single γ′ phase and ε + γ′ dual-phase layer. More importantly, it was found that the wear resistance was closely related to the phase constitution of nitrided layer under different loads, the best wear resistance under light load of 200 g was obtained for the sample with ε + γ′ dual-phase layer due to the highest hardness; whereas the best wear resistance under heavy load of 400 g was obtained for the sample with single γ′ phase layer due to its excellent combination of hardness and toughness. Meanwhile, the mechanisms of phase constitution control and wear behaviors of nitrided layer under different loads were revealed.</p>

physics, applied,materials science, coatings & films