Abstract:A numerical simulation method is presented to evaluate the controlling issues of property for heavy forgings such as the evolvement of void defect and the evolution of microstructure. In order to reveal the multi-scale effect of macroscopic plastic deformation as well as the stress state on the volumetric evolvement of tiny voids stochastically distributed in the forgings,a model calculating the void volumetric change through macroscopic stress and strain field is investigated by using a representative volume element model. By integrating the model with finite element method,with the void fraction is assumed,the void volume evolvement at each element can be evaluated simultaneously with the simulation of forging process. So it can be used to assess the degree of void closure for the forging materials with shrinkage cavity and porosity. For the simulation of microstructure evolution,a cellular automata modeling is investigated and applied to a rotor steel. According to the micro-and macroscopic relationship among "strain,dislocation density,dynamic recrystallization and flow stress",the dynamic recrystallization process is simulated and the R-grain size and kinetics percentage are obtained. By combining these property-related models with thermo-mechanical finite element method,the numerical technique is established to simulate the forging process and predict the deformed shape and evolution of void defect and grain size. Besides that,according to the features of incremental forming typically used for heavy forgings,a fast finite element method is developed by using rigid degree of freedom condensation technique. This method is an effective tool for simulating and optimizing the forming process.

Forming of Inner Faults Originating from Inclusions in the Heavy Forgings and the Process of Forging Control

The Mechanism of Faults Originating from Inclusions in the Plastic Deformation Processes of Heavy Forging

Inner crack with inclusion and forging process control of heavy forgings

Mechanism for Development of Faults Originating from Compound Inclusions in the Forging Process of 30cr2ni4mov Heavy Ingots

Microstructure Refinement and Crack Initiation in the Forging Process

Defect Analysis of Complex-Shape Aluminum Alloy Forging

Analysis of laminated crack defect in the upsetting process of heavy disk-shaped forgings

Multi-scale simulation for the forming of a heavy vessel head considering the evolution of defects and microstructure

Failure control on hydroforming process of thin-walled aluminum alloy with complex surface covers

Study on the Bonding Condition of Inner Crack Defects in Heavy Forgings

Defects analysis of aluminum alloy disk forging with complex shape in isothermal forging

Computer Modeling of Property-controlled Forging Process for Heavy Forgings

Principle of Internal Defects Recovery in Processes of High Temperature Plastic Deformation

Formation criterion of fissure defects in the inner wall of the radial forged steel tube

A General Simulation Technology for Forging with Considering the Evolution of Voids, Grains and Cracks

The Effect of the Microstructure Formed in the Forging–Healing Process on the Mechanical Properties of Heavy Forgings

Prediction of ductile cracking in the titanium alloy forging process

Analysis and Control of Car Door Inner Panel Forming Fracture Based on Experience Knowledge and Numerical Simulation

Investigations on Failure-to-fracture Mechanism and Prediction of Forming Limit for Aluminum Alloy Incremental Forming Process

Modeling and Numerical Simulation Research on Hollow Steel Ingot Forging Process of Heavy Cylinder Forging

Formation mechanism and control of a kind of pit-shaped defect in Cf53 rolled products