Abstract:The mechanically-alloyed amorphous 2Si-B-3C-N powder was hot pressed at 1900°C for 30mins in argon. A small amount (5mol.%) of AlN and ZrO2 was added to investigate their effect on the sintering process, microstructure and properties of the 2Si-B-3C-N ceramic. XRD, SEM, TEM and property testing results show that, the addition of AlN or ZrO2 promotes the sintering process of the 2Si-B-3C-N composite powder, accelerates the crystallization and grain growth, and improves the density and mechanical properties of the prepared ceramic. Under an axial pressure of 80MPa and a gas pressure of 8bar, significant densification occurs to the 2Si-B-3C-N ceramic free from any additives just when the temperature is higher than 1830°C. The addition of AlN and ZrO2 decreases this critical temperature to about 1760°C and 1730°C, respectively. As a result, for the prepared bulk ceramic, the average grain size is increased from 80nm to 200nm and 250nm, the relative density is enhanced from 88.7% to 96.9% and 97.7%, and the bending strength is improved from 331MPa to 416MPa and 575MPa, respectively. Careful investigation reveals that in the prepared bulk ceramic, AlN forms solid solution with SiC, and ZrO2 exists in the form of t-ZrO2 and m-ZrO2 nanocrystals. Thus, the addition of AlN and ZrO2 may facilitate the atomic diffusion, the grain growth and the densification process of the 2Si-B-3C-N ceramic in difficult ways.

Processing and properties of Al2O3-ZrO2(3Y)-SiC nanocomposites

Mechanical Properties and Microstructure of Sic-Zro2(3y)-Al2o3 Nanocomposites

Fabrication and Mechanical Properties of Nano-SiC-Oxide Composites

Preparation and properties of intragranular Al2O3-SiC nanocomposites

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Preparation and properties of β-CaSiO3/ZrO2 (3Y) nanocomposites

Microstructure and Properties of Hot Pressed Zr2(Al(Si))4C5/SiC Composites

Densification and Mechanical Properties of Si3N4/SiC Nanocomposite Using Si-Nitrided Si3N4 Powder

Effect of Al2O3 addition on mechanical properties of SiC-platelet/Y-TZP composites

In Situ Synthesis, Mechanical Properties, and Oxidation Resistance of (sic+zrb2)/zr3[al(si)]4c6 Composites

Influence of SiC particle size on microstructure and mechanical properties of Al2O3-SiC nanocomposites

Spark plasma sintering and mechanical properties of Al_2O_3-ZrO_2 nanocomposites

Precipitation behavior and mechanical properties of Al-Zn-Mg-Cu matrix nanocomposites: Effects of SiC nanoparticles addition and heat treatment

Enhanced Mechanical Properties, Thermal Shock Resistance and Oxidation Resistance of Si2BC3N Ceramics with Zr-Al Addition

Effect of AlN and ZrO2 on the Microstructure and Property of the 2Si-B-3c-n Ceramic

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Preparation and Mechanical Properties of Al2O3–15wt.%ZrO2 Composites

Effects of residual stress and intragranular particles on mechanical properties of hot-pressed Al2O3/SiC ceramic composites

Aqueous Processing, Hot-Pressing and Mechanical Properties of Silicon Carbide with Al2O3 and Y2O3

Preparation And Properties Of Dense Zrb2 Composite Reinforced By Elongated Sic And Al3bc3 Grains