Abstract:The composite ceramics between Al 2 O 3 (6 mol%MgO) and ZrO 2 (4 mol%Y 2 O 3 ) were prepared in the Al 2 O 3 (6 mol%MgO added: ZrO 2 (4 mol%Y 2 O 3 added) ratios of 20:80, 35:65, 50:50, 65:35 and 80:20. All of samples were sintered using two stage sintering routes with the first temperature (T 1 ) at 1600 °C for 30 min and the second temperature (T 2 ) at 1450 °C for 5 h. The physical properties were characterized from percentage of shrinkage and bulk density. It can be found their tend to decrease with Al 2 O 3 (6 mol%MgO) content increase. XRD patterns were showed combination main phase of rhombohedral of Al 2 O 3 and monoclinic, cubic, tetragonal of ZrO 2 . Rietveld refinement were used to calculate the percentage of phase composition. All of samples were revealed weight percentage of main composition as m -ZrO 2 c -ZrO 2 t -ZrO 2 and r - Al 2 O 3 in different ratios. It can be found, sample with more content of ZrO 2 was showed higher weight percentage of c -ZrO 2 . The high intensity of Al 2 O 3 peak was appeared from sample with high Al 2 O 3 concentration. SEM micrographs reveal morphology of grain such as grain shape and size of grains. The average grain size value is between 0.81 and 1.07 μm and the size of grain tend to increase with high Al 2 O 3 content. EDX technique were analyzed element compositions of Al 2 O 3 (6 mol%MgO): ZrO 2 (4 mol%Y 2 O 3 ) and EDX spectra were showed wt.% element of Al, Zr, O Y and Mg which is confirmed molecular formular. Moreover, EDX method is identified square shape of Al 2 O 3 (6 mol%MgO) and round shape of ZrO 2 (4 mol%Y 2 O 3 ). The mechanical properties were measured by Vickers and Knoop hardness that were used for calculating the fracture toughness value. It can be found that the optimum mechanical properties were obtained from composite ceramic of 0.35Al 2 O 3 (6 mol%MgO): 0.65ZrO 2 (4 mol%Y 2 O 3 ) which is showed the highest of fracture toughness value about 0.38 GPa.m 1/2 .

Preparation and Mechanical Properties of Al2O3–15wt.%ZrO2 Composites

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Preparation and Characterization of Alumina Zirconia Composite Ceramics

Reaction mechanisms and properties of in situ porous Al2O3-ZrO2-mullite composites

Preparation of high-strength alumina-zirconia fibers by the sol-gel method combined with two-step sintering processes

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

Sintering Behavior and Mechanical Properties of Alumina-Coated Zirconia Ceramics

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Temperature‐dependent mechanical and oxidation behavior of in‐situ formed ZrN/ZrO2‐containing Si3N4‐based composite

Prospects for improving the mechanical properties of an aluminum-zirconium composite by adding ultrafine Al2O3 powder synthesized by nitrate combustion

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

ZrSiO4 toughed Al2O3 ceramics prepared by reaction sintering

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Sinterability of ZrSiO4/α-Al2O3 Mixed Powders

Preparation and properties of ZrP2O7 matrix composites with high silica fibers reinforcement

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

The Effect of Nano-Al2O3 on Sintering Behavior and Mechanical Property of ZrO2 Ceramics