Growth Of Bi2sr2cacu2o8 Single-Crystals From Bi-Rich Melts
Wb Wu,Fq Li,Yb Jia,G Zhou,Yt Qian,Qn Qin,Yh Zhang
DOI: https://doi.org/10.1016/0921-4534(93)90767-k
IF: 1.534
1993-01-01
Physica C: Superconductivity and its Applications
Abstract:High-quality Bi2Sr2CaCu2O8 single crystals with dimensions up to 15 x 4 x 0.05 mm3 were grown from the starting composition Bi2+xSr2CaCu2Oy, where x = 0, 0. 1, 0.2, 0.3, 0.4, 0.5, 0.6 and 0.7. Different amounts of Bi2O3 in excess are included in each crystal growth run to act as flux for the growth and the optimum concentrations of the flux amount have been found. Structure characterization of a high-quality 2212 free crystal of 5 x 1.8 x 0.02 MM3 was conducted by the (001), (h00) and (0k0) X-ray diffractions, using a rotating anode diffractometer, and the back-reflection Laue photograph. It is found that melting incongruency is the main problem encountered in the growth of large and pure-phase single crystals from Bi2O3-rich melts and we have shown that, for x = 0.8, crystals of 2212 phase and crystals of 2201 phase coexisting with CuO are obtained from the two segregated parts of the Bi-rich melts.