Superconductivity and Raman Scattering Inbi2sr2ca1…

X. H. Chen,Min Yu,Guojian Qian,Z. S. Liu,Lei Cao,Jie Zou,Cunyi Xu

DOI: https://doi.org/10.1103/physrevb.57.5082

1998-01-01

Abstract:Polycrystalline samples of ${\mathrm{Bi}}_{2}{\mathrm{Sr}}_{2}{\mathrm{Ca}}_{1\ensuremath{-}x}{\mathrm{Pr}}_{x}{\mathrm{Cu}}_{2}{\mathrm{O}}_{y}$ $(x=0\ensuremath{-}1)$ have been characterized by x-ray diffraction, resistivity, and Raman scattering measurements. Superconducting samples $(x<0.6)$ show a $T$-linear resistivity, and $d\ensuremath{\rho}/dT$ is consistent with the Drude model. Upon replacement of Ca by Pr, an increase of the excess oxygen incorporated into ${\mathrm{Bi}}_{2}{\mathrm{O}}_{2}$ double layers causes an elongation of the $\mathrm{Bi}\ensuremath{-}\mathrm{O}{(2)}_{\mathrm{Sr}}$ bond length, which is an important factor, resulting in softening of the $\mathrm{O}{(2)}_{\mathrm{Sr}}$ ${A}_{g}$ phonon. A downshift of the $\mathrm{O}{(1)}_{\mathrm{Cu}}$ ${B}_{1g}$ phonon with increasing $x$ in Pr-doped Bi2212 arises from an increase of the average ${\mathrm{Ca}}^{2+}/{\mathrm{Pr}}^{3+}$ radius. The origin of this softening is the same as that in Y-doped Bi2212, Y123, and Y124 systems.