The Magnetic Properties of Cu-doped Sm–Fe–Si–C Ribbons Prepared by Melt Spinning

HW Zhang,SY Zhang,BG Shen,LG Zhang

DOI: https://doi.org/10.1063/1.367280

IF: 2.877

1998-01-01

Journal of Applied Physics

Abstract:We studied magnetic properties of Cu-doped Sm–Fe–Si–C compounds with the Th2Zn17-type structure prepared by melt spinning. Substituting small amounts of Cu for Fe does not change the unit cell volume v, Curie temperature TC, and magnetocrystalline field HA of these materials, while the saturation magnetization Ms decreases slightly. A drastic increase in the coercivity has been observed upon Cu addition. The highest intrinsic coercivity μ0iHc=1.32 T and 1.47 T at room temperature was obtained in Sm2Fe14CuSi2C and Sm2Fe14CuSi2C1.5 ribbons prepared at a wheel speed of 15 m/s, respectively. The large coercivity can result from the atoms Cu precipitated in the grain boundaries, which has a pinning domain wall effect. The coercivity mechanism is mainly controlled by the nucleation of reversed domains. The microstructural parameter αk and the averaged local effective demagnetization factor Neff were derived from the temperature dependence of coercivity.