Abstract:In this work, the WC-Cr2(C, N)-Co nanocomposites were synthesized by using the one-pot carbothermal reduction nitridation hydrothermal precursor method. The preparation mechanisms, including phase and morphology evolutions, were investigated by differential thermal analysis (TG-DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and thermodynamic analysis. The results showed that phase evolution, with temperature increasing, follows the sequences of (amorphous phase, WO2.72) → (CoWO4, WO2.72, WO2, CrWO3) → (WO2, CoWO4, Co6W6C, CrWO3) → (W2C, Co3W3C, WC) → (WC, W2C, Co3W3C) → (WC, Co, Co3W3C trace amount). Through comparing different heat treatment conditions, the powder particle size was more easily affected by temperature than holding time. The higher temperatures or longer time holding resulted in the aggregation of powder particles. Finally, WC-Cr2(C, N)-Co nanopowders with about 60 nm were obtained at 1050 °C for 1 h under the N2 flow of 1 L/min with the oxygen content of 0.22 wt% and the free carbon content of 0.19 wt%. The TEM elements mapping revealed that Cr distributes uniformly with WC grains, Co and WC grains are combined well. The surface of WC-Cr2(C, N)-Co determined by XPS is mainly composed of W, Co, Cr, C, N, and O. The spark plasma sintering (SPS) sintered WC-Cr2(C, N)-Co composite shows a nanocrystalline microstructure with the average grain size ∼170 nm, and the excellent comprehensive mechanical properties with the Vickers hardness 1730 Kg·mm−2 and fracture toughness 11.5 MPa·m1/2, respectively.

Preparation of Nanocrystalline Tungsten Powder and Study of Its Sinterability

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

High-pressure Preparation of Bulk Tungsten Material with Near-Full Densification and High Fracture Toughness

Towards pressureless sintering of nanocrystalline tungsten

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Effect of Ball Milling Parameters on Properties of Nano-Sized Tungsten Powder via Mechanochemical Processing

Effect of ZrC nano-powder addition on the microstructure and mechanical properties of binderless tungsten carbide fabricated by spark plasma sintering

Formation of Nanocrystalline Fcc Phase by Mechanically Driven Crystallization

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Preparation of ti-al based nanophase composite powder by mechanical alloying

Development of Tungsten-Based Materials by Different Sintering Techniques

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Fabrication of nanocrystalline and ultra-hard tungsten alloy by dual particles dispersion strengthening

Binderless nanocrystalline tungsten carbide with enhanced hardness induced by high-pressure sintering

Main Influential Factors of Preparing Nano-tungsten Powder Using High Energy Ball Mill

Ultrafine Grained Bulk Ceramic Composites Consolidated from Nanostructured Composite Powders by Pressure Less Sintering

Densification and microstructure evolution of W-TiC-Y2O3 during spark plasma sintering

Tungsten heavy alloy: Nano-crystallinity and alloying induced low temperature sintering, microstructure and mechanical properties

Pressureless Two-Step Sintering of Ultrafine-Grained Tungsten

Ultrafine Binderless WC-based Cemented Carbides with Varied Amounts of AlN Nano-Powder Fabricated by Spark Plasma Sintering

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites