Abstract:Silver vanadate (AgVO3) nanowires were synthesized by hydrothermal method and self-lubricating NiAl/Mo-AgVO3 composites were fabricated by powder metallurgy technique. The composition and microstructure of NiAl/Mo-based composites were characterized and the tribological properties were investigated from room temperature to 900°C. The results showed that NiAl/Mo-based composites were consisted of nanocrystalline B2 ordered NiAl matrix, Al2O3, Mo2C, metallic Ag and vanadium oxide phase. The appearance of metallic Ag and vanadium oxide phase can be attributed to the decomposition of AgVO3 during sintering. Wear testing results confirmed that NiAl/Mo-based composites have excellent tribological properties over a wide temperature range. For example, the friction coefficient and wear rate of NiAl/Mo-based composites containing AgVO3 were significantly lower than the composites containing only metallic Mo or AgVO3 lubricant when the temperature is above 300°C, which can be attributed to the synergistic lubricating action of metallic Mo and AgVO3 lubricants. Furthermore, Raman results indicated that the composition on the worn surface of NiAl-based composites was self-adjusted after wear testing at different temperatures. For example, Ag3VO4 and Fe3O4 lubricants were responsible for the improvement of tribological properties at 500°C, AgVO3, Ag3VO4 and molybdate for 700°C, and AgVO3 and molybdate for 900°C of NiAl-based composites with the addition of metallic Mo and AgVO3.

Study on the High Temperature Tribological Properties of Ni-Cr Based Alloys Containing MoS2

Excellent Tribological Performance at Elevated Temperatures and Associated Mechanisms of Novel AlCoCrFeNi-MoS2 Solid Self-Lubricating Composite

Synergetic Lubricating Effect of MoS2 and Ti3SiC2 on Tribological Properties of NiAl Matrix Self-Lubricating Composites over a Wide Temperature Range

Influence of Mo contents on the tribological properties of CrMoN/MoS2 coatings at 25–700 °C

Dependence of High Temperature Tribological Performance of Mos2-Based Composites on Type of Oxides

Investigation of the elevated temperature tribological property and wear mechanism of Fe‐15Cu‐0.8C materials containing Mo‐coated MoS2 powders

High temperature tribological behaviors and wear mechanisms of NiAl-MoO3/CuO composite coatings

Tribological Behaviors of NiAl Based Self-Lubricating Composites Containing Different Solid Lubricants at Elevated Temperatures

Friction and Wear Characteristics of Hot-Pressed NiCr–Mo/MoO 3 /ag Self-Lubrication Composites at Elevated Temperatures Up to 900 °C

Microstructure and tribological properties evolution of Ni-Mo-SrSO 4 composites as a function of Mo contents at different temperatures

Effect of MoS2 on the Tribological Properties of in Situ Fe3Al-20 Wt% Al2O3-4 Wt% Cr Composites

Tribological Properties of Self-Lubricating NiAl/Mo-based Composites Containing AgVO3 Nanowires

Tribological Properties of Ni-based Self-Lubricating Composites with Addition of Silver and Molybdenum Disulfide

Tribological Performance Of Ni3al Self-Lubricating Composites With Different Content Of Tic At Elevated Temperature

Fabrication and High-Temperature Tribological Properties of Self-Lubricating NiCr–BaMoO 4 Composites

Wear and Friction of TiAl Matrix Self-Lubricating Composites against Si3N4 in Air at Room and Elevated Temperatures

Wear Properties of NiAl Based Materials

Study on Tribological Performances of MoS2 Coating at High Temperature

High-temperature compressive properties and tribological behaviour of Mo2NiB2–Ni cermets

Microstructure and Tribological Properties of Reactive Hot Pressed TiN–TiB2 Composites Incorporated with or Without MoSi2 from Room Temperature to 800°C

Influence of Mo doping on the tribological behavior of Ti3AlC2 ceramic at different temperatures