High-temperature compressive properties and tribological behaviour of Mo2NiB2–Ni cermets

L. Zhang,Z.F. Huang,Y.P. Shen,K.M. Li,Z. Cao,Y.X. Jian,Z.J. Ren

DOI: https://doi.org/10.1016/j.ceramint.2019.06.058

IF: 5.532

2019-01-01

Ceramics International

Abstract:The present work investigated the high-temperature compressive strength and tribological behaviours of Mo2NiB2–Ni cermets from 25 to 900 °C. Mo2NiB2–Ni cermets with four different Ni additions were first fabricated successfully and then tested. The results show that cermets with Ni/B 1.1 have the best compressive strength of 531.8 MPa at 900 °C and superior strength retention at high temperature. With the best high-temperature compressive strength, Mo2NiB2–Ni cermets with Ni/B 1.1 are used as pins with Si3N4 disks in a tribological test. The wear rate of Mo2NiB2–Ni cermets gradually increases as the temperature increases from 25 to 900 °C, while the friction coefficient shows the opposite trend. Within the entire testing temperature range, the friction coefficient decreases, and the minimum friction coefficient is obtained at 900 °C. The decline of the friction coefficient is attributed to the self-lubricating oxidation tribolayer covering the worn surface. Moreover, the dominant wear mechanism changes from abrasive wear to oxidation wear as the temperature exceeds 600 °C.