Preparation and application evaluation of La2O3-doped Y2O3 crucible materials for melting TiAl alloys
Haoran Li,Yan Liu,JinJing Yang,Ming Yuan,Anle Sun,Tiesong Lin,Xuejian Liu,Zhengren Huang
DOI: https://doi.org/10.1016/j.ceramint.2022.02.113
IF: 5.532
2022-06-01
Ceramics International
Abstract:A new La2O3-doped Y2O3 crucible materials was fabricated and evaluated by TiAl alloys melting test. Microstructure and properties of the La2O3-doped Y2O3 ceramics were systemically investigated. In addition, interfacial reaction mechanism of the La2O3-doped Y2O3 crucible materials and TiAl alloys, together with oxygen content of TiAl alloys were discussed. Solid solution of La3+ in the crystal lattice of Y2O3 significantly improved sintering properties of the La2O3-doped Y2O3 crucible materials and decreased the open porosity. Compared with pure Y2O3, when adding 15 wt% La2O3, the open porosity and strength retention ration after thermal shock test of the La2O3-doped Y2O3 crucible materials changed from 10.8% to 3.9% and from 64% to 78%, respectively. The interfacial reaction between La2O3-doped Y2O3 crucible materials and TiAl alloys belongs to physical dissolution, and no reaction products were found during the melting of TiAl alloys. When using the 15 wt% La2O3-doped Y2O3 crucible materials to melt TiAl alloys, oxygen content of the TiAl ingot declined to 530 ppm, which was only one fourth of that using pure Y2O3 materials.
materials science, ceramics