New insight into precipitation of Al3Zr and correlative effect on recrystallization behavior in a rapidly-solidified Al-Zn-Mg-Cu-Zr alloy
Zhiping Wang,Hongyu Xiao,Wei Chen,Yugang Li,Jiwei Geng,Xianfeng Li,Peikang Xia,Mingliang Wang,Dong Chen,Haowei Wang
DOI: https://doi.org/10.1016/j.matchar.2022.112142
IF: 4.537
2022-09-01
Materials Characterization
Abstract:The influence of temperature of first-step pretreatment on the precipitation and crystal structure of Al3Zr in a spray-formed (SFed) Al-Zn-Mg-Cu alloy was systematically explored. With different first-step pretreatments, the microstructure evolutions during hot extrusion and solution treatment were studied. The results show that pretreatment before hot-working is necessary for rapidly-solidified Al-Zn-Mg-Cu alloy and temperature of first-step pretreatment is crucial for stabilizing microstructures. In detailed, the homogenous nucleation of L12 Al3Zr is limited at low first-step temperature (<250°C), while the transformation from L12 Al3Zr to D023 Al3Zr is simulated and high first-step temperature (≥420°C). The crystallographic orientation relationship between D023 Al3Zr precipitate (P) and Al matrix is recognized as: [001]Al//[011]P, (200)Al//(011 ̄)P, (020)Al//(200)P, which is different from the previous works. When the first-step temperature is 250–350°C, the dispersed η-Mg(Zn,Al,Cu)2 phases formed during spray forming can act as heterogeneous nucleation sites of Al3Zr precipitation. The recrystallization resistance of SFed Al-Zn-Mg-Cu alloy during solution treatment is markedly enhanced by an optimized pretreatment of 250°C@36 h + 470°C@24 h.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing