Abstract:Erbium-doped silica glasses were made by sol-gel process. Intensive photoluminescence (PL) spectra from the Er-doped silica glasses at room temperature were measured. A broadband peak at 1535 ma, corresponding to the I-4(13/2)-I-4(15/2) transition, its full width at half-maximum (FWHM) of 10 nm, and a shoulder at 1546 nm in the PL spectra were observed. At lower temperatures, main line of 1535 nm and another line of 1552 Mn instead of 1546 nm appear. So two types of luminescence centers must exist in the samples at different temperature. The intensity of main line does not decrease obviously with increasing temperature. By varying the Er ion concentration in the range of 0.2 wt% - 5wt%, the highest photoluminescence intensity was obtained at 0.2wt% erbium doped concentration. Luminescence intensity decreases with increasing erbium concentration. Cooperative upconversion was used to explain the concentration quenching of luminescence from silica glass with high erbium concentration. Extended X-ray absorption fine structure measurements were carried out. It was found that the majority of the erbium impurities in the glasses have a local structure of eight first neighbor oxygen atoms at a mean distance of 0.255 nm, which is consistent with the typical coordination structure of rare earth ion.

[Investigation on the Luminescence Properties of Er Ions in Er-doped Sol-Gel Silica Glasses].

Preparation And Characterization Of Erbium Doped Sol-Gel Silica Glasses

Room temperature photoluminescence from Zr4+-doped sol–gel silica

Room Temperature Photoluminescence Property of Boron-Doped Sol–gel Silica

Visible Room-Temperature Photoluminescence of Ge-doped SiO2 Glasses Fabricated by a Sol–gel Process

Investigation on the Fluorescence Properties of Er-doped Sol-Gel Silica Glasses

Study of Eu3+-doped Luminescence Glasses Prepared by a Sol-Gel Process

Luminescence of Bi3+ Ions and Energy-Transfer from Bi3+ Ions to Eu3+ Ions in Silica Glasses Prepared by the Sol-Gel Process

Spectroscopic Studies of Rare Earth Ions in Silica Glasses Prepared by the Sol-Gel Process

Research on optical properties of Yb3+/Er3+ co-doped oxy-fluoride glass

PREPARATION AND OPTICAL PROPERTIES OF Er-DOPED SILICA GLASS

Optical Absorption and Emission Properties of Er3+ Doped Mixed Alkali Borosilicate Glasses

Preparation and Luminescence of Er3+ Doped Oxyfluoride Glass Ceramics Containing LaF3 Nanocrystals

Upconversion Luminescence Property of Er3+ and Yb3+ Co-doped Germanium Silicate Glass

Phase Transformation and Photoluminescence Properties of Er Silicate Films by Sol-Gel Method

Preparation and Quantum Cutting Luminescence Properties of Er3+/Yb3+Co-doped Oxyfluoride Glass Ceramics

Correlation Of Efficient Luminescence With Crystal Structures Of Y-Er2si2o7 And Alpha-Er2si2o7 In Er-Doped Silicon Oxide Films

Spectroscopic Properties Of Er3+ Doped Glass Ceramics Containing Sr2gdf7 Nanocrystals

Photoluminescence and Its Physical Mechanism of Er/Yb Co-Doped Borate-Silicate Glass

Luminescence at 1.53 Μm for a New Er3+-doped Transparent Oxyfluoride Glass Ceramic

Control of the Formation and Luminescent Properties of Polymorphic Erbium Silicates on Silicon