Abstract:Erbium-doped silica glasses were made by sol-gel process. Intensive photoluminescence (PL) spectra from the Er-doped silica glasses at room temperature were measured. A broadband peak at 1535 ma, corresponding to the I-4(13/2)-I-4(15/2) transition, its full width at half-maximum (FWHM) of 10 nm, and a shoulder at 1546 nm in the PL spectra were observed. At lower temperatures, main line of 1535 nm and another line of 1552 Mn instead of 1546 nm appear. So two types of luminescence centers must exist in the samples at different temperature. The intensity of main line does not decrease obviously with increasing temperature. By varying the Er ion concentration in the range of 0.2 wt% - 5wt%, the highest photoluminescence intensity was obtained at 0.2wt% erbium doped concentration. Luminescence intensity decreases with increasing erbium concentration. Cooperative upconversion was used to explain the concentration quenching of luminescence from silica glass with high erbium concentration. Extended X-ray absorption fine structure measurements were carried out. It was found that the majority of the erbium impurities in the glasses have a local structure of eight first neighbor oxygen atoms at a mean distance of 0.255 nm, which is consistent with the typical coordination structure of rare earth ion.

PREPARATION AND OPTICAL PROPERTIES OF Er-DOPED SILICA GLASS

Preparation And Characterization Of Erbium Doped Sol-Gel Silica Glasses

Research on optical properties of Yb3+/Er3+ co-doped oxy-fluoride glass

Spectroscopic Studies of Rare Earth Ions in Silica Glasses Prepared by the Sol-Gel Process

[Investigation on the Luminescence Properties of Er Ions in Er-doped Sol-Gel Silica Glasses].

Preparation and Spectroscopic Properties of Er3+-doped High Silica Glass Fabricated by Sintering Nanoporous Glass

Spectral properties of Er3+ doped high silica glass

Optical Absorption and Emission Properties of Er3+ Doped Mixed Alkali Borosilicate Glasses

Specltal Properties of Er3+ Doped High Silica Glass

Spectroscopic Properties Of Er3+ Doped Glass Ceramics Containing Sr2gdf7 Nanocrystals

STUDY ON PREPARATION AND SPECTRAL PROPERTIES OF Er3+-DOPED TELLURITE GLASS

Spectroscopic Properties and Thermal Stability of Er3+-Doped Fluoride Lead Silicate Glasses

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

Preparation and Luminescence of Er3+ Doped Oxyfluoride Glass Ceramics Containing LaF3 Nanocrystals

Spectroscopic Properties of Er3+–Yb3+ Co-Doped Glass Ceramics Containing BaF2 Nanocrystals

Spectroscopic Properties and Judd-Ofelt Theory Analysis of Er3+-Doped Heavy Metal Oxyfluoride Silicate Glass

Luminescence at 1.53 Μm for a New Er3+-doped Transparent Oxyfluoride Glass Ceramic

Optical Properties of Er3+-singly Doped and Er3+/Yb3+-codoped Novel Oxyfluoride Glasses

Optical Characterization of Ultraviolet Laser Photosensitive Er3+-doped Bismuth-Silicate Glasses

Optical transitions in Er3+ doped lead germanate glasses