Abstract:Abstract High density polyethylene (HDPE) is widely used in city water and gas piping system and even in nuclear engineering for its excellent properties in flexibility, impact resistance, aging and corrosion resistance, reliable connection, long service life. It is generally believed that the typical failure mode of PE pipe under long-term static pressure load is the slow crack growth (SCG) caused by creep crack initiation (CCI) and creep crack growth (CCG), which is a kind of quasi-brittle failure. Scratching often occurs during PE pipe installation due to the drag of pipe without any protection, which would leave axial cracks as the initial defect. This would harm the long term performance of pressurized HDPE pipe. In the present work, the creep crack kinetics was experimentally determined in term of C* integral, and then CCG behavior of PE pipe with axial semi-elliptical crack was discussed. With the help of a CARE electronic universal testing machine and DIC displacement measuring system, creep tests are performed with smooth bar specimen of PE100 pipe parent material. And the stationary creep law parameters were determined. The crack opening displacement (COD) rates were determined by creep cracking test with cracked round bar specimen. With the help of compliance calibration tests, the COD curves were changed into crack propagation curves and the creep crack kinetics was eventually determined in term of C* integral. By assuming an semi-elliptical crack front with nearly the same C* integral, the creep crack propagation was predicted with the determined crack kinetics. And the allowable initial crack size was also determined for the PE pipe discussed. Compared with that determined in terms of SIF, current study yields much margin for the allowable initial crack.

Determination of Critical Pressure for Full Scale Pe Gas Pipe Using Small Scale Test Results

Material Fracture Toughness Determination for Polyethylene Pipe Materials Using Small Scale Test Results

Determination of material fracture toughness by a computational/experimental approach for rapid crack propagation in PE pipe

Simulation of A Small-Scale Steady State Test

Viscoelastic and Damage Model of Polyethylene Pipe Material for Slow Crack Growth Analysis

A Numerical Study on the High-Velocity Impact Behavior of Pressure Pipes

Study of Dynamic Fracture Behavior of Pressure Pipes

Dynamic Ductile Fracture Toughness Test and Numerical Simulation for Ultra-High Pressure Gas Pipelines

Analysis of Dynamic Fracture Mechanisms in Gas Pipelines

The Toughness-Induced Crack Deceleration Mechanism on Ultra-High Pressure Steel Gas Pipelines

CCG of PE100 and Life Prediction of PE Pipe With Axial Semi-Elliptical Crack

Safety Test Research of Pressure Pipes Containing Incomplete Welding Defects

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Steady State Analysis for Dynamic Crack Propagation in Gas Pipelines

Burst Pressure of Pipelines with Plastic Anisotropy under Combined Internal and External Pressures

The recent development of analysis methodology for rapid crack propagation and arrest in gas pipelines

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Driving Force and Deformation Analysis for Dynamic Crack Propagation in Gas Pipelines under Different Boundary Conditions

The FEM Simulation and Full-Scale Blast Tests for Crack Deceleration in Gas Pipeline

The performance and causes of failure of polyethylene pipes subjected to constant and fluctuating internal pressure loadings

An engineering model for rapid crack propagation along fluid pressurized plastic pipe