Effect of Temperature on Superplastic Deformation Behavior of 2198 Al–Cu–Li Alloy
Zengyu Wang,Zhiting Yang,Senbao Jiang,Yusheng Wang,Yao Chen,Xifeng Li,Qudong Wang
DOI: https://doi.org/10.1016/j.msea.2023.145988
2024-01-01
Abstract:Al-Li alloy possesses remarkable advantages such as low density, high specific strength and specific elastic modulus, making it an exceptional aerospace structural material with considerable application potential. However, Al-Li alloy suffers from poor formability, which restricts its broader engineering applications. Alternatively, superplastic forming at high temperatures is widely applied for producing such components. Temperature is a key factor affecting the thermal deformation properties of Al-Li alloy. In this study, tensile tests of 2198 Al-Cu-Li alloy were conducted at different temperatures, and dedicated characterizations were performed to reveal the underlying mechanisms responsible for the hot deformation behavior. Results reveal that three distinct stages are observed in the superplastic deformation process of this alloy. Specifically, in the initial lowtemperature range (400 degrees C-450 degrees C), incomplete dynamic recrystallization (DRX), accompanied by grain rotation and elongation plays a dominant role in the hot deformation mechanism. In the middle temperature stage (450 degrees C-500 degrees C), both DRX and grain boundary sliding (GBS) occur. At the high-temperature stage (500 degrees C-550 degrees C), diffusion creep emerges as the prominent mechanism. Moreover, optimum superplasticity is achieved at 500 degrees C, which results from a synergistic combination of several factors, including grain refinement by DRX, an increased fraction of high-angle grain boundaries (HAGBs), reduced dislocation density and weak texture.