Preparation of SO42 -/TiO2-Al2O3 Soild Superacid Catalyst and Its Catalytic Activity for Borneol Synthesis
Helin WANG,Lihong JIANG,Yaming WANG,Xingxing JIAO,Deng PAN
DOI: https://doi.org/10.11896/j.issn.1005-023X.2017.022.009
2017-01-01
Abstract:A series of sulphated Al2 O3-TiO2 mixed oxides were prepared by sol-gel and dipping process and used as catalysts in synthesis of borneol .The structure and properties of SO42 - /TiO2-Al2O3 solid superacid catalysts were characterized by XRD ,NH3-TPD ,FT-IR ,Py-FTIR ,XPS ,SEM techniques ,and relationship between the catalytic performance and the structure was explored . The optimal condition for the preparation of the catalyst was obtained as follows :n(TiO2 )/n(Al2O3 )= 1:2 ,concentration of impregnation 1 mol/L ,calcination temperature of the catalysts 500 ℃ .Meanwhile ,the effects of the dosage of level of catalyst , molar ratio of α-pinene to oxalic acid ,reaction time on borneol synthesis reaction was investigated .The results showed that when the dosage of level of catalyst was 6% and molar ratio of α-pinene to oxalic acid was 1:0 .4 ,by using the program temperature heating method (65 ℃-1 h ,75 ℃-4 h ,90 ℃-1 h) ,i .e .the optimized condition ,the resultant solid superacid SO42 - /TiO2-Al2O3 catalyst performed the best catalytic effect to borneol synthesis reaction ,asα-pinene was completely converted and high selectivity of borneol (58 .63% yield) was achieved . After 6 times reuse , the catalyst still maintained good performance—α-pinene conversion rate unchanged ,yield of borneol decreased by 2 .99% .