Preparation, Surface Acidity and Catalytic Esterification Activity of Solid Acid S2O2-8/TiO2-La2O3
Jie-Yu He,Hui Wang,De-Zhong Liao,Yun-Kang Jin
DOI: https://doi.org/10.2991/icmse-16.2016.17
2016-01-01
Abstract:Solid acid S 2 O 2- 8 /TiO 2 -La 2 O 3 (STL) was prepared by calcination at high temperature using complex oxide of TiO 2 doped La 2 O 3 as the supporter , and anion S 2 O 2- 8 as the accelerant.The catalytic synthesis of n-butyl propanoate over STL was selected as the probe reaction to examine its catalytic esterification activity.The preparing conditions of STL were optimized via Taguchi method.The acidic structure, species and strength of STL were characterized by FTIR directly, FTIR spectrum of pyridine adsorbed on its surface and Hammett indicator, respectively.The esterification product was characterized by 1 HNMR and FTIR.The experimental results showed that the optimum preparation conditions were as follows: molar ratio of Ti to La at 5:1, (NH 4 ) 2 S 2 O 8 solution concentration of 2.0 mol•L -1 and calcination temperature of 500 o C. STL belonged to the solid superacid (Ho=-13.75)with Brönsted acid sites.The esterification rate of above probe reaction could reach 99.3% at the reaction time of 90 min. IntroductionAs an effective and eco-friendly heterogeneous catalyst, solid acid SO 2- 4 /M x O y prepared by using transition metal oxide (M x O y ) and sulphuric acid as the supporter and accelerant, respectively, has been highly concerned by many scholars in the latest decades [1,2].Compared with traditional liquid acids (e.g.H 3 PO 4 , H 2 SO 4 ) as homogeneous catalyst, SO 2- 4 /M x O y as the heterogeneous catalyst offers many advantages in chemical process, such as no corrosion to equipment, simple post treatment for reactions, high acidic strength and high catalytic activity [3,4].Solid acid SO 2- 4 /M x O y shows a great potential for application in biodiesel production[1,5] and many other catalytic reactions, such as esterification[6], alkylation [7], isomerization[8] and acetylation [9].In recent years, there are some reports that transition metal oxide doped rare earth as the supporter of solid acid SO 2- 4 /M x O y can significantly improve its catalytic properties in many reactions, such as selectivity, activity and thermal stability [10][11][12].Anion S 2 O 2- 8 can be employed as the accelerant to replace SO 2- 4 for prepared S 2 O 2- 8 /M x O y [13].However, the titanium source for the preparation of SO 2- 4 /M x O y containing TiO 2 overwhelmingly was titanium tetrachloride or butyl titanate [11,12].S 2 O 2- 8 /M x O y prepared by employing titanium sulfate, complex oxide of TiO 2 doped La 2 O 3 and anion S 2 O 2- 8 as the titanium source, supporter and accelerant, respectively, has not been reported in the research field of solid acid yet.In our work, the precursor of complex oxide of TiO 2 doped La 2 O 3 was firstly prepared by a low-temperature deposition method with titanium sulfate as the titanium source; and then STL was prepared by calcinations at high temperature after the as-prepared precursor was impregnated by using (NH 4 ) 2 S 2 O 8 solution as the accelerant source; finally the acidic structure, species, strength and the catalytic esterification activity of STL were studied as well.