Spectroscopic properties and energy transfer in Er–Tm co-doped bismuth silicate glass
Xin Wang,Zhilan Li,Kefeng Li,Lei Zhang,Jimeng Cheng,Lili Hu
DOI: https://doi.org/10.1016/j.optmat.2013.06.020
IF: 3.754
2013-10-01
Optical Materials
Abstract:In this paper, we investigate the spectroscopic properties of and energy transfer processes in Er–Tm co-doped bismuth silicate glass. The Judd–Ofelt parameters of Er3+ and Tm3+ are calculated, and the similar values indicate that the local environments of these two kinds of rare earth ions are almost the same. When the samples are pumped at 980nm, the emission intensity ratio of Tm:3F4→3H6 to Er:4I13/2→4I15/2 increases with increased Er3+ and Tm3+ contents, indicating energy transfer from Er:4I13/2 to Tm:3F4. When the samples are pumped at 800nm, the emission intensity ratio of Er:4I13/2→4I15/2 to Tm:3H4→3F4 increases with increased Tm2O3 concentration, indicating energy transfer from Tm:3H4 to Er:4I13/2. The rate equations are given to explain the variations. The microscopic and macroscopic energy transfer parameters are calculated, and the values of energy transfer from Er:4I13/2 to Tm:3F4 are found to be higher than those of the other processes. For the Tm singly-doped glass pumped at 800nm and Er–Tm co-doped glass pumped at 980nm, the pumping rate needed to realize population reversion is calculated. The result shows that when the Er2O3 doping level is high, pumping the co-doped glass by a 980nm laser is an effective way of obtaining a low-threshold ∼2μm gain.
materials science, multidisciplinary,optics