Abstract:Single-phase cubic pyrochlore-typed Bi1.5MgNb1.5O7 (BMN) dielectric ceramics were synthesized at temperatures of 1050–1200°C by solid-state reaction method. Their atomic-scale microstructures and dielectric properties were investigated. X-ray diffraction patterns revealed that the BMN ceramics had an average cubic pyrochlore structure, whereas the Raman spectra indicated that they had an essentially cubic symmetry with small local deviations at the A and O' sites of the cubic pyrochlore structure. This was confirmed by selected electron area diffraction (SAED) patterns, where the reflections of {442} (not allowed in the cubic pyrochlore with Fd3¯m symmetry) were clearly observed. SEM and TEM images revealed that the average grain size was increased with the sintering temperature, and an un-homogeneous grain growth was observed at high temperatures. HRTEM images and SAED patterns revealed the single-crystalline nature of the BMN ceramic grains. Energy dispersive spectroscopy (EDS) elemental mapping studies indicated that the compositional distributions of Bi, Mg, Nb and O elements in the ceramic grains were homogenous, and no elemental precipitation was observed at the grain boundary. Quantitative EDS data on ceramic grains revealed the expected cationic stoichiometry based on the initial composition of Bi1.5MgNb1.5O7. Dielectric constants of all the BMN samples exhibited almost frequency independent characteristic in the frequency range of 102–106Hz, and the highest value was 195 for the BMN ceramics sintered at sintered at 1150°C with the highest bulk density. The dielectric losses were stable and less than 0.002 in the frequency range of 102–105Hz. The high dielectric constants of the present BMN samples can be ascribed to the local atomic deviations at the A and O' sites from the ideal atomic positions of the pyrochlore structure, which affect the different polarization mechanisms in the BMN ceramics, and which in turn enhance the dielectric constants of the BMN ceramic samples.

Synthesis and Dielectric Properties of New Compounds with Pyrochlore Type Structure

Structure, IR spectra and dielectric properties of Bi2O3–ZnO–SnO2–Nb2O5 quarternary pyrochlore

STRUCTURE AND DIELECTRIC PROPERTIES OF BZN-BASED CERAMICS WITH Zn2+ IN A SITE SUBSTITUTED BY K+,La3+

Structure, Dielectric and Optical Properties of Bi1.5+xZnNb1.5O7+1.5x Pyrochlores

Structures, Phase Transformations, and Dielectric Properties of Pyrochlores Containing Bismuth

Dielectric Properties of Pyrochlore (Bi1.5zn0.5)(nb0.5m1.5)o-7 (m=ti, Sn, Zr, and Ce) Dielectrics

Study of structure and dielectrc properties of non-stoichiometric Bi 2 O 3 -ZnO-Nb 2 O 5 ceramics

Observations on structural evolution and dielectric properties of oxygen-deficient pyrochlores

Structure and dielectric properties of pyrochlore-fluorite biphase ceramics in the Bi<sub>2</sub>O<sub>3</sub>-ZnO-Nb<sub>2</sub>O<sub>5</sub> system

Phase Structure and Dielectric Properties of Bi2O3‐ZnO‐Nb2O5‐Based Dielectric Ceramics

Atomic-scale microstructures, Raman spectra and dielectric properties of cubic pyrochlore-typed Bi1.5MgNb1.5O7 dielectric ceramics

Structure and dielectric properties of pyrochlore–fluorite biphase ceramics in the Bi 2 O 3 –ZnO–Nb 2 O 5 system

Synthesis and Large Cell Structure of Eu2Cu2/3Nb4/3O7

Effect of Ca substitution on phase compositions and dielectric properties of Bi2O3-ZnO-Nb2O5 pyrochlore ceramics

Synthesis, structure, and characterization of new low-firing microwave dielectric ceramics: (Ca1-3xBi2x Phi(x))MoO4

Structure, Dielectric and Optical Properties of Bi1.5ZnNb1.5−xTaxO7 Cubic Pyrochlores

Structures and Electric Properties of Cubic Bismuth Based Pyrochlore Thin Films Grown by Pulsed Laser Deposition

Synthesis, Structure and Dielectric Properties of Bi2O3-ZnO-CaO-Nb2O5ceramics

Dielectric properties and microstructural characterization of cubic pyrochlored bismuth magnesium niobates

Effect of La2O3 substitutions on structure and dielectric properties of Bi2O3–ZnO–Nb2O5-based pyrochlore ceramics

Synthesis and dielectric properties of pyrochlore solid solutions in the Bi2O3-ZnO-Nb2O5-TiO2 system