Structure, Dielectric and Optical Properties of Bi1.5ZnNb1.5−xTaxO7 Cubic Pyrochlores
Qian Wang,Hong Wang,Xi Yao
DOI: https://doi.org/10.1063/1.2735409
IF: 2.877
2007-01-01
Journal of Applied Physics
Abstract:The crystal structure, dielectric properties, and optical properties of Bi1.5ZnNb1.5−xTaxO7 (BZNT,x=0, 0.5, 1.0, 1.5) pyrochlore ceramics were investigated. The structures of the BZNT ceramics were identified as cubic pyrochlores and the lattice parameters decreased with x increasing. Thermogravimetric analysis were carried out suggesting that there are no Bi and/or Zn volatility at the sintered temperatures. All the samples exhibit low dielectric losses and high resistivities. Substituting Nb5+ by Ta5+ leads to smaller permittivity and temperature coefficient of permittivity. The relaxation behavior of the BZNT ceramics was observed at lower temperatures less than −100 °C. The peaks of the dielectric constant in conjunction with the peaks of dielectric loss shift to lower temperatures with x increasing and frequency decreasing, revealing that the active energy became higher according to Arrhenius law. The bands in Raman spectra were assigned to symmetry species. Ta5+ and Nb5+ with large polarizability induced a distortion of the BO6 octahedra leading to a dynamic disorder. The fundamental absorption edges in the absorption spectra show obvious blueshift when x increasing, suggesting that the band gap energy increases. The four compounds show optical absorption at wavelength shorter than 450 nm. This means that the compounds have the ability to respond to the wavelengths in the visible light region.