Crystal structures and microwave dielectric properties of (1-x)Ba(Zn1/3Nb2/3)O3 − xBaWO4 (0 ≤ x ≤ 0.25) ceramics
Sen Peng,Yu Zhang,Lei Xiao,Lianwen Deng,Yanbin Xie,Tulin Yi
DOI: https://doi.org/10.1088/1402-4896/ad137d
2023-12-08
Physica Scripta
Abstract:The (1-x)Ba(Zn1/3Nb2/3)O3-xBaWO4 (0 ≤ x ≤ 0.25) ceramics were manufactured by the conventional solid-phase reaction process, and the effects of BaWO4 addition on the phase composition, crystal structure, microstructure, and microwave dielectric properties were investigated. X-ray diffraction (XRD), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) were implemented to explore the phase composition, crystal structure and chemical states of the samples, respectively. According to XRD analysis, the main phase of the samples was assigned as Ba(Zn1/3Nb2/3)O3 (BZN), while the secondary phases contained Ba5Nb4O15 and BaWO4. Scanning electron microscopy (SEM) photographs suggested the average grain size (AG) firstly increased and then decreased with the replacement of W6+ ions to Nb5+ ions in BZN. Due to the substitution of W6+ for Nb5+, the apparent density was largely affected by the content of liquid phases. The microwave dielectric properties were closely associated with the secondary phases and apparent density. Finally, (1-x)Ba(Zn1/3Nb2/3)O3-xBaWO4 (x = 0.15) ceramics sintered at 1325 °C for 4 h had excellent microwave dielectric properties with εr = 33.11, Q×f = 90,479 GHz, and τf = +0.86 ppm/°C.
physics, multidisciplinary