Abstract:The transformation-assisted consolidation under pressure has been demonstrated to be a promising method to fabricate the nano or submicron polycrystalline ceramic materials. The high pressure suppresses the long-range diffusion of the atoms and, consequently, restrains the grain coarsening. The new phases produced at high pressure could show finer grains under the appropriate thermodynamic conditions, which are not subject to the grain size of the raw materials. Ceramic materials exhibit the existence of the transformations under certain thermodynamic conditions and the formation of new phases generally undergoes the nucleation and growth. In the present work, monoclinic microcrystal ZrO2 with average grain size of 2 µm and Y2O3 with average grain size of 50 nm were mixed in molar ratio of 97∶3. The preparation of the samples was carried out by sintering at 5.5 GPa and temperatures of 800–1700 °C using the high pressure cubic cell, and the sample characterization was performed via the X-ray diffraction, scanning electron microscope and transmission electron microscopy. It was found that the monoclinic and submicron tetragonal composite polycrystalline ZrO2 in bulk is obtained under high pressure and high temperature. The average grain size of tetragonal ZrO2 fabricated at 1200, 1400, 1600 and 1700 °C is (145±62) nm, (246±165) nm, (183±62) nm and (245±107) nm, respectively. The synthesis of the fine-grained polycrystalline materials by the transformation under high pressure can solve the problems of agglomeration, adsorption and grain coarsening caused by the nanopowders as the starting materials in the conventional approach, which would be an alternative route to fabricate the fine-grained polycrystalline materials with the enhanced performances.

Preparation of Nano T-Zro2 Particle by the Integrated Process of High-Gravity Field and Hydrothermal Crystallization

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Preparation and properties of yttria-stabilized tetragonal phase zirconia nano-ceramics by high gravity

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

Nano-sized Amorphous Cu–Zr Alloy Particles Prepared by Mechanochemical Reaction

Preparation and Self-assembly of Zirconia Nanoparticles Via Hydrothermal Method

Template-Free Hydrothermal Synthesis of Octahedron-, Diamond-, and Plate-like ZrO2 Mono-Dispersions

Synthesis and Pyrolysis Evolution of Glucose-Derived Hydrothermal Precursor for Nanosized Zirconium Carbide

The Hydrothermal Synthesis of ZrO<sub>2</sub> Nanoparticles and Their Optical Absorption Properties

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method

Effect of Particle Size on Phase Structure of Zro2 Produced by Hydrolysis of Zrocl2 Solution

Monoclinic zirconium oxide nanostructures synthesized by a hydrothermal route

Synthesis of Yttrium Oxide Nanocrystal Via Solvothermal Process

Preparation of amorphous ZrO2 powders by hydrothermal-assisted sol-gel method