Abstract:Cement solidification is essential to reduce heavy metal leaching from industrial sludge and make it recyclable. This paper studied the effect of aggregate grading optimized by sludge containing heavy metal of different particle sizes on the performance of baking-free sludge bricks, which was mixed with industrial sludge cured by both micro-silica fume and cement. First, the gradation of fine natural aggregates was adjusted according to the Fuller curve. Fine aggregates in baking-free bricks were replaced by artificially processed sludge with particle sizes of 0.15 mm ~0.3 mm and 2.36 mm ~4.75 mm. In this case, a mixed proportion scheme was designed. Then, the strength, water absorption, porosity, and heavy metal leaching were measured. With the help of nuclear magnetic resonance (NMR) and scanning electron microscopy (SEM), the phase and pore structures were observed. The test results showed that: (1) Sludge can replace part of the fine aggregates to make baking-free bricks, resulting in the reduction of the strength of baking-free bricks, but the strength still meets the standard strength requirements of GB/T 21,144-2007. (2) When fine aggregates are partly replaced by sludge with finer particle sizes, baking-free sludge bricks exhibit higher strength, lower water absorption, better pore structures and microphase structure, and stronger solidification of heavy metals, the leaching number of heavy metals meets the standard requirements of GB5085.3-2007, which will be provided support for actual industrial production.Implications: Cement solidification is an essential means to reduce the heavy metal leaching from industrial sludge and make it recyclable. This paper studied sludge containing heavy metal of different particle sizes on the performance of baking-free sludge bricks. This paper analyzed the compressive strength, porosity and water absorption of baking-free bricks mixed with sludge of different partical sizes, and adopted the NMR to characterize the pores of baking-free bricks, and the SEM to observe the baking-free bricks resultants and the interfacial transition zone (ITZ). The heavy metal leaching test verified the environmental benefits of baking-free bricks mixed with sludge instead of aggregates. There not only make full use of solid wastes, but also thus minimizing pollution to the environment, which provide support for actual industrial production and a reference for studying industrial sludge recycling technology.

Experimental Study on the Detoxification of Chrome Sludge by Making Bricks

Recycling of Heavy Metal Contaminated River Sludge into Unfired Green Bricks: Strength, Water Resistance, and Heavy Metals Leaching Behavior – A Laboratory Simulation Study

Experimental study on preparation of unburned and non autoclaved brick from neutralization slag of lead zinc smelting wastewater

The characteristics and resource utilization of chromium-containing electroplating sludge

Research on the Synthesis of Sintered Bricks Using River Sludge for the Resource Utilization

Preparation, characteristics and mechanisms of the composite sintered bricks produced from shale, sewage sludge, coal gangue powder and iron ore tailings

The migration and transformation of chromium during co-processing of cement raw meal mixed with chrome-polluted soil

Comprehensive Performance Study of Aluminum Ash and Calcium Carbide Slag for Brick Making under Ultra-High Pressure

Using restored heavy metal contaminated soil as brick making material: Risk analysis upon different scenarios, considering the completeness of bricks

Effect of industrial sludge particle size on the performance of baking-free sludge bricks

Treatment of chromium-containing sludge using sintering and ironmaking combined technology: A risk-reducing strategy for environmental impact

Characteristic pollutants risk assessment of modified manganese residue utilization in sintered product

Lightweight bricks manufactured from ground soil, textile sludge, and coal ash

The reuse of waste glass to enhance strength during the introduction of municipal sewage sludge in shale brick manufacturing

DETOXICATION OF SLAGE CONTAINING CHROMIUM BY MICROWAVE IRRADIATION

Influence of chlorine on co-processing of hazardous wastes in brick kilns

Effect of Waste Addition Points on the Chromium Leachability of Cement Produced by Co-Processing of Tannery Sludge

Utilizing Industrial Sludge Ash in Brick Manufacturing and Quality Improvement

Fabrication of Lead–Zinc Tailings Sintered Brick and Its Effect Factors Based on an Orthogonal Experiment

Preparation of Sintered Brick with Aluminum Dross and Optimization of Process Parameters

Using Bayer red mud and calcium fluoride sludge to make co-fired bricks