Abstract:High-hardness hydrophobic anti-reflection thin films were prepared by a mixture of acid-catalyzed and alkali-catalyzed sols using tetraethyl silicate (TEOS) and methyltriethoxysilane (MTES) bisilicon sources as precursors. The alkali-catalyzed SiO 2 sol and the acid-catalyzed SiO 2 sol modified with aliphatic alcohol ethoxylated ether (AEO) were synthesized firstly, and then the acid-catalyzed SiO 2 sol was doped into the alkali-catalyzed SiO 2 sol in a certain ratio to prepare the anti-reflection thin films. The effects of the doping ratio of acid-catalyzed SiO 2 sol on the microstructures and properties of thin films were investigated. The experimental results show that both the transmittance and the contact angle increase and then decrease with the increasing of the doping ratio of acid-catalyzed SiO 2 sol, and the surface hardness and adhesion are gradually enhanced. When the doping ratio of acid-catalyzed SiO 2 sol is 30%, the average transmittance of the reflectance-reducing film is 92.51% in the wavelength range of 400–1100 nm, which is 5.17% higher than that of the blank glass. The water contact angle of the reflectance-reducing film is up to 92°, and the adhesion of the film is the highest level 0. After 100 h of UV exposure, the transmittance of the film was reduced by 1.1%.

Preparation of SiO2 antireflective film by a base/acid two-step catalyzed sol-gel process

Preparation of Antireflective Coatings with High Transmittance and Enhanced Abrasion-Resistance by a Base/acid Two-Step Catalyzed Sol–gel Process

Sol-gel Preparation of Hydrophobic Silica Antireflective Coatings with Low Refractive Index by Base/acid Two-Step Catalysis.

Sol-gel Preparation of Self-Cleaning SiO2-TiO2/SiO2-TiO2 Double-Layer Antireflective Coating for Solar Glass

Preparation of Octyltrimethoxysilane Modified SiO$lt;inf$gt;2$lt;/inf$gt; Hydrophobic Antireflective Coating

Preparation of high hardness hydrophobic SiO2 anti reflective thin films from mixed acid catalyzed and alkali catalyzed sols

Design and Preparation of SiO2/TiO2/SiO2-TiO2 Antireflective Coatings with Excellent Abrasion-resistance and Transmittance Via Sol-Gel Process

Sol-gel Preparation of Anti-Fogging SiO2/SiO2-TiO2 Double-layer Antireflective Coating

Study on the SiO2 Antireflective Coatings Prepared from Sol-Gel Process

Sol-gel Preparation of a Silica Antireflective Coating with Enhanced Hydrophobicity and Optical Stability in Vacuum

Sol-gel derived SiO2 antireflective (AR) coating used in solar cells

Study on the Properties and Structure of SiO2 Anti-reflective Coating Prepared by Stepped Base/Acid Catalyzed Process

Stability Of The Silica Sols Prepared By Acid/Base Two-Step Catalytic Sol-Gel Process

Design and preparation of SiO 2/TiO 2/SiO 2-TiO 2 antireflective coatings with excellent abrasion-resistance and transmittance via sol-gel process

Design and Preparation of Sio2/Sio2-Tio2 Antireflective Coating with Excellent Environmental Resistance

The Study of the Silicon Dioxide Anti-Reflection Film Prepared by the Sol-Gel Method

Preparation of Highly Transparent and Wear-Resistant SiO2 Coating by Alkali/acid Dual Catalyzed Sol–gel Method

Preparation of silica antireflective films for solar energy application

Broadband Antireflective Coatings with Different Film Designs by Sol-Gel Method

Sol−Gel Preparation of PDMS/Silica Hybrid Antireflective Coatings with Controlled Thickness and Durable Antireflective Performance

Low-Temperature Preparation of SiO2/Nb2O5/TiO2–SiO2 Broadband Antireflective Coating for the Visible via Acid-Catalyzed Sol–Gel Method